An optimal cure process to minimize residual void and optical birefringence for a LED silicone encapsulant

Min Jae Song, Kwon Hee Kim, Gil Sang Yoon, Hyung Pil Park, Heung Kyu Kim

Research output: Contribution to journalArticle

6 Citations (Scopus)

Abstract

Silicone resin has recently attracted great attention as a high-power Light Emitting Diode (LED) encapsulant material due to its good thermal stability and optical properties. In general, the abrupt curing reaction of the silicone resin for the LED encapsulant during the curing process induces reduction in the mechanical and optical properties of the LED product due to the generation of residual void and moisture, birefringence, and residual stress in the final formation. In order to prevent such an abrupt curing reaction, the reduction of residual void and birefringence of the silicone resin was observed through experimentation by introducing the multi-step cure processes, while the residual stress was calculated by conducting finite element analysis that coupled the heat of cure reaction and cure shrinkage. The results of experiment and analysis showed that it was during the three-step curing process that the residual void, birefringence, and residual stress reduced the most in similar tendency. Through such experimentation and finite element analysis, the study was able to confirm that the optimization of the LED encapsulant packaging process was possible.

Original languageEnglish
Pages (from-to)4088-4104
Number of pages17
JournalMaterials
Volume7
Issue number6
DOIs
Publication statusPublished - 2014 Jan 1

ASJC Scopus subject areas

  • Materials Science(all)

Fingerprint Dive into the research topics of 'An optimal cure process to minimize residual void and optical birefringence for a LED silicone encapsulant'. Together they form a unique fingerprint.

  • Cite this