Bubble nucleation during devolatilization of polymer melts

Alexander Yarin, D. Lastochkin, Y. Talmon, Z. Tadmor

Research output: Contribution to journalArticle

16 Citations (Scopus)

Abstract

Devolatilization of different types of polymer melts was studied experimentally and theoretically. The experimental work was carried out in a 'falling-strand'-type apparatus built especially for this study. Polymer samples after devolatilization were examined by scanning electron microscopy. The micrographs obtained showed that strong nucleation of bubble nuclei occurs first in the vicinity of existing primary microbubbles. These bubble nuclei (secondary nuclei) form blisters (microbubbles) growing under appropriate conditions. The growth is controlled by momentum transfer and diffusion. The microbubbles then coalesce leading to formation of large voids and foaming of the polymer strands. The key parameter, the critical bubble radius triggering the process of growth, was assessed from the micrographs. The time dependence of the concentration of the residual styrene (dissolved gas) in polystyrene melt was determined by gas chromatography. A theoretical model of stress-enhanced secondary nucleation in polymer melts during their devolatilization was developed. It shows that nucleation proceeds due to the growth of initially existing gas bubbles, when a sample is exposed to vacuum. In the vicinity of the bubbles homogeneous nucleation proceeds at an accelerated rate, because it is strongly enhanced by mechanical degradation of polymer macromolecules. The rate of devolatilization was calculated and compared with the experimental data. Theoretical results agreed with the experimental data rather good, although no adjustable parameters characteristic of some of the existing nucleation models were involved.

Original languageEnglish
Pages (from-to)2590-2605
Number of pages16
JournalAICHE Journal
Volume45
Issue number12
Publication statusPublished - 1999 Dec 1
Externally publishedYes

Fingerprint

Polymer melts
Polymers
Nucleation
Microbubbles
Growth
Gases
Styrene
Momentum transfer
Polystyrenes
Blister
Vacuum
Macromolecules
Gas chromatography
Gas Chromatography
Electron Scanning Microscopy
Theoretical Models
Degradation
Scanning electron microscopy

ASJC Scopus subject areas

  • Biotechnology
  • Chemical Engineering(all)
  • Mechanical Engineering
  • Environmental Engineering
  • Polymers and Plastics

Cite this

Yarin, A., Lastochkin, D., Talmon, Y., & Tadmor, Z. (1999). Bubble nucleation during devolatilization of polymer melts. AICHE Journal, 45(12), 2590-2605.

Bubble nucleation during devolatilization of polymer melts. / Yarin, Alexander; Lastochkin, D.; Talmon, Y.; Tadmor, Z.

In: AICHE Journal, Vol. 45, No. 12, 01.12.1999, p. 2590-2605.

Research output: Contribution to journalArticle

Yarin, A, Lastochkin, D, Talmon, Y & Tadmor, Z 1999, 'Bubble nucleation during devolatilization of polymer melts', AICHE Journal, vol. 45, no. 12, pp. 2590-2605.
Yarin A, Lastochkin D, Talmon Y, Tadmor Z. Bubble nucleation during devolatilization of polymer melts. AICHE Journal. 1999 Dec 1;45(12):2590-2605.
Yarin, Alexander ; Lastochkin, D. ; Talmon, Y. ; Tadmor, Z. / Bubble nucleation during devolatilization of polymer melts. In: AICHE Journal. 1999 ; Vol. 45, No. 12. pp. 2590-2605.
@article{9de4364a21d344e3a0bf5dc2bed197b6,
title = "Bubble nucleation during devolatilization of polymer melts",
abstract = "Devolatilization of different types of polymer melts was studied experimentally and theoretically. The experimental work was carried out in a 'falling-strand'-type apparatus built especially for this study. Polymer samples after devolatilization were examined by scanning electron microscopy. The micrographs obtained showed that strong nucleation of bubble nuclei occurs first in the vicinity of existing primary microbubbles. These bubble nuclei (secondary nuclei) form blisters (microbubbles) growing under appropriate conditions. The growth is controlled by momentum transfer and diffusion. The microbubbles then coalesce leading to formation of large voids and foaming of the polymer strands. The key parameter, the critical bubble radius triggering the process of growth, was assessed from the micrographs. The time dependence of the concentration of the residual styrene (dissolved gas) in polystyrene melt was determined by gas chromatography. A theoretical model of stress-enhanced secondary nucleation in polymer melts during their devolatilization was developed. It shows that nucleation proceeds due to the growth of initially existing gas bubbles, when a sample is exposed to vacuum. In the vicinity of the bubbles homogeneous nucleation proceeds at an accelerated rate, because it is strongly enhanced by mechanical degradation of polymer macromolecules. The rate of devolatilization was calculated and compared with the experimental data. Theoretical results agreed with the experimental data rather good, although no adjustable parameters characteristic of some of the existing nucleation models were involved.",
author = "Alexander Yarin and D. Lastochkin and Y. Talmon and Z. Tadmor",
year = "1999",
month = "12",
day = "1",
language = "English",
volume = "45",
pages = "2590--2605",
journal = "AICHE Journal",
issn = "0001-1541",
publisher = "American Institute of Chemical Engineers",
number = "12",

}

TY - JOUR

T1 - Bubble nucleation during devolatilization of polymer melts

AU - Yarin, Alexander

AU - Lastochkin, D.

AU - Talmon, Y.

AU - Tadmor, Z.

PY - 1999/12/1

Y1 - 1999/12/1

N2 - Devolatilization of different types of polymer melts was studied experimentally and theoretically. The experimental work was carried out in a 'falling-strand'-type apparatus built especially for this study. Polymer samples after devolatilization were examined by scanning electron microscopy. The micrographs obtained showed that strong nucleation of bubble nuclei occurs first in the vicinity of existing primary microbubbles. These bubble nuclei (secondary nuclei) form blisters (microbubbles) growing under appropriate conditions. The growth is controlled by momentum transfer and diffusion. The microbubbles then coalesce leading to formation of large voids and foaming of the polymer strands. The key parameter, the critical bubble radius triggering the process of growth, was assessed from the micrographs. The time dependence of the concentration of the residual styrene (dissolved gas) in polystyrene melt was determined by gas chromatography. A theoretical model of stress-enhanced secondary nucleation in polymer melts during their devolatilization was developed. It shows that nucleation proceeds due to the growth of initially existing gas bubbles, when a sample is exposed to vacuum. In the vicinity of the bubbles homogeneous nucleation proceeds at an accelerated rate, because it is strongly enhanced by mechanical degradation of polymer macromolecules. The rate of devolatilization was calculated and compared with the experimental data. Theoretical results agreed with the experimental data rather good, although no adjustable parameters characteristic of some of the existing nucleation models were involved.

AB - Devolatilization of different types of polymer melts was studied experimentally and theoretically. The experimental work was carried out in a 'falling-strand'-type apparatus built especially for this study. Polymer samples after devolatilization were examined by scanning electron microscopy. The micrographs obtained showed that strong nucleation of bubble nuclei occurs first in the vicinity of existing primary microbubbles. These bubble nuclei (secondary nuclei) form blisters (microbubbles) growing under appropriate conditions. The growth is controlled by momentum transfer and diffusion. The microbubbles then coalesce leading to formation of large voids and foaming of the polymer strands. The key parameter, the critical bubble radius triggering the process of growth, was assessed from the micrographs. The time dependence of the concentration of the residual styrene (dissolved gas) in polystyrene melt was determined by gas chromatography. A theoretical model of stress-enhanced secondary nucleation in polymer melts during their devolatilization was developed. It shows that nucleation proceeds due to the growth of initially existing gas bubbles, when a sample is exposed to vacuum. In the vicinity of the bubbles homogeneous nucleation proceeds at an accelerated rate, because it is strongly enhanced by mechanical degradation of polymer macromolecules. The rate of devolatilization was calculated and compared with the experimental data. Theoretical results agreed with the experimental data rather good, although no adjustable parameters characteristic of some of the existing nucleation models were involved.

UR - http://www.scopus.com/inward/record.url?scp=0033396440&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=0033396440&partnerID=8YFLogxK

M3 - Article

VL - 45

SP - 2590

EP - 2605

JO - AICHE Journal

JF - AICHE Journal

SN - 0001-1541

IS - 12

ER -