Characteristics of BaTiO3-coated Ag powders directly prepared by spray pyrolysis

You Na Ko, Jung Hyun Kim, Yun Chan Kang

Research output: Contribution to journalArticle

1 Citation (Scopus)

Abstract

Spherical BaTiO3-coated Ag powders with dense structures were directly prepared by spray pyrolysis. Ag powder with 1wt% BaTiO3 has particles of 0.53μm mean diameter. BaTiO3 had good properties for coating Ag powders: it decreased the sintering of the Ag powder at temperatures between 700 and 900°C. Complete melting of pure Ag powder, forming dense Ag thick film, occurred at 700°C. Whereas at this temperature, partial melting of the 1wt% BaTiO3-coated Ag powder occurred, forming Ag thick film with a porous structure. The pure Ag thick film shrunk 45% at 900°C. However, the thick films formed from 1 and 5wt% BaTiO3-coated Ag powder had respective shrinkages of 31 and 21%, respectively at 900°C. The sheet resistances of the Ag thick films formed from the 1wt% BaTiO 3-coated Ag powder were 7.54, 4.93 and 4.09mΩ/sq at firing temperatures of 700, 800 and 900°C, respectively.

Original languageEnglish
Pages (from-to)15-20
Number of pages6
JournalJournal of the Ceramic Society of Japan
Volume120
Issue number1397
DOIs
Publication statusPublished - 2012 Jan

Keywords

  • Ag powder
  • Barium titanate
  • Electrode material
  • Spray pyrolysis

ASJC Scopus subject areas

  • Ceramics and Composites
  • Chemistry(all)
  • Condensed Matter Physics
  • Materials Chemistry

Fingerprint Dive into the research topics of 'Characteristics of BaTiO<sub>3</sub>-coated Ag powders directly prepared by spray pyrolysis'. Together they form a unique fingerprint.

  • Cite this