Characteristics of MgO-coated alkaline earth selenide phosphor prepared by spray pyrolysis

Wonkeun Chung, Hyunchul Jung, Chang Hun Lee, Sung Hyun Kim

Research output: Contribution to journalArticle

2 Citations (Scopus)

Abstract

Spherical submicron sized Eu2+-activated SrSe and CaSe alkaline earth selenide phosphorswere prepared by ultrasonic spray pyrolysis. The particle size decreased with decreasing precursor solution concentration, while the pyrolysis temperature had a negligible effect on the particles size and morphology. Due to the d-f transition of Eu2+, SrSe:Eu2+ and CaSe:Eu2+ showed the broad band emission with maximum peaks at 565 and 608 nm, respectively. Further, the addition of 10 wt% NH4Cl flux helped to enhance the emission intensity by reducing the surface defects. MgO coating on selenide phosphor surface effectively improved the moisture stability without a significant loss in the luminescence intensity. 5-10 wt% MgO-coated SrSe: Eu2+, and CaSe:Eu2+ nearly retained their initial luminescence intensity under water condition.

Original languageEnglish
Pages (from-to)98-103
Number of pages6
JournalThin Solid Films
Volume546
DOIs
Publication statusPublished - 2013 Nov 1

Fingerprint

Spray pyrolysis
selenides
Phosphors
phosphors
pyrolysis
sprayers
Luminescence
Earth (planet)
Particle size
Surface defects
luminescence
Pyrolysis
Moisture
Ultrasonics
surface defects
Fluxes
moisture
Coatings
Water
ultrasonics

Keywords

  • Alkaline earth selenide
  • MgO coating
  • Phosphor
  • Spray pyrolysis

ASJC Scopus subject areas

  • Electronic, Optical and Magnetic Materials
  • Materials Chemistry
  • Metals and Alloys
  • Surfaces, Coatings and Films
  • Surfaces and Interfaces

Cite this

Characteristics of MgO-coated alkaline earth selenide phosphor prepared by spray pyrolysis. / Chung, Wonkeun; Jung, Hyunchul; Lee, Chang Hun; Kim, Sung Hyun.

In: Thin Solid Films, Vol. 546, 01.11.2013, p. 98-103.

Research output: Contribution to journalArticle

Chung, Wonkeun ; Jung, Hyunchul ; Lee, Chang Hun ; Kim, Sung Hyun. / Characteristics of MgO-coated alkaline earth selenide phosphor prepared by spray pyrolysis. In: Thin Solid Films. 2013 ; Vol. 546. pp. 98-103.
@article{b057337fc35645749339297b23594392,
title = "Characteristics of MgO-coated alkaline earth selenide phosphor prepared by spray pyrolysis",
abstract = "Spherical submicron sized Eu2+-activated SrSe and CaSe alkaline earth selenide phosphorswere prepared by ultrasonic spray pyrolysis. The particle size decreased with decreasing precursor solution concentration, while the pyrolysis temperature had a negligible effect on the particles size and morphology. Due to the d-f transition of Eu2+, SrSe:Eu2+ and CaSe:Eu2+ showed the broad band emission with maximum peaks at 565 and 608 nm, respectively. Further, the addition of 10 wt{\%} NH4Cl flux helped to enhance the emission intensity by reducing the surface defects. MgO coating on selenide phosphor surface effectively improved the moisture stability without a significant loss in the luminescence intensity. 5-10 wt{\%} MgO-coated SrSe: Eu2+, and CaSe:Eu2+ nearly retained their initial luminescence intensity under water condition.",
keywords = "Alkaline earth selenide, MgO coating, Phosphor, Spray pyrolysis",
author = "Wonkeun Chung and Hyunchul Jung and Lee, {Chang Hun} and Kim, {Sung Hyun}",
year = "2013",
month = "11",
day = "1",
doi = "10.1016/j.tsf.2013.05.028",
language = "English",
volume = "546",
pages = "98--103",
journal = "Thin Solid Films",
issn = "0040-6090",
publisher = "Elsevier",

}

TY - JOUR

T1 - Characteristics of MgO-coated alkaline earth selenide phosphor prepared by spray pyrolysis

AU - Chung, Wonkeun

AU - Jung, Hyunchul

AU - Lee, Chang Hun

AU - Kim, Sung Hyun

PY - 2013/11/1

Y1 - 2013/11/1

N2 - Spherical submicron sized Eu2+-activated SrSe and CaSe alkaline earth selenide phosphorswere prepared by ultrasonic spray pyrolysis. The particle size decreased with decreasing precursor solution concentration, while the pyrolysis temperature had a negligible effect on the particles size and morphology. Due to the d-f transition of Eu2+, SrSe:Eu2+ and CaSe:Eu2+ showed the broad band emission with maximum peaks at 565 and 608 nm, respectively. Further, the addition of 10 wt% NH4Cl flux helped to enhance the emission intensity by reducing the surface defects. MgO coating on selenide phosphor surface effectively improved the moisture stability without a significant loss in the luminescence intensity. 5-10 wt% MgO-coated SrSe: Eu2+, and CaSe:Eu2+ nearly retained their initial luminescence intensity under water condition.

AB - Spherical submicron sized Eu2+-activated SrSe and CaSe alkaline earth selenide phosphorswere prepared by ultrasonic spray pyrolysis. The particle size decreased with decreasing precursor solution concentration, while the pyrolysis temperature had a negligible effect on the particles size and morphology. Due to the d-f transition of Eu2+, SrSe:Eu2+ and CaSe:Eu2+ showed the broad band emission with maximum peaks at 565 and 608 nm, respectively. Further, the addition of 10 wt% NH4Cl flux helped to enhance the emission intensity by reducing the surface defects. MgO coating on selenide phosphor surface effectively improved the moisture stability without a significant loss in the luminescence intensity. 5-10 wt% MgO-coated SrSe: Eu2+, and CaSe:Eu2+ nearly retained their initial luminescence intensity under water condition.

KW - Alkaline earth selenide

KW - MgO coating

KW - Phosphor

KW - Spray pyrolysis

UR - http://www.scopus.com/inward/record.url?scp=84885291916&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=84885291916&partnerID=8YFLogxK

U2 - 10.1016/j.tsf.2013.05.028

DO - 10.1016/j.tsf.2013.05.028

M3 - Article

AN - SCOPUS:84885291916

VL - 546

SP - 98

EP - 103

JO - Thin Solid Films

JF - Thin Solid Films

SN - 0040-6090

ER -