TY - JOUR
T1 - Communication
T2 - Solubility of nitrogen in high manganese steel (HMnS) melts: Interaction parameter between Mn and N
AU - Shin, Jae Hong
AU - Lee, Joonho
AU - Min, Dong Joon
AU - Park, Joo Hyun
PY - 2011/12
Y1 - 2011/12
N2 - Nitrogen solubility in Fe-Mn melts was measured using a N 2 bubbling and sampling method at temperatures from 1823 K to 1923 K (1550 °C to 1650 °C) for manganese content to about 25 mass pct. The effect of temperature on the nitrogen solubility was well described based on the thermodynamic behavior of Fe-Mn system. Furthermore, the interaction parameter between Mn and N was evaluated as a function of temperature. The present results can be used in thermodynamic analyses of the formation of nitride compounds such as AlN or TiN in high manganese steel melts for example, transformation induced plasticity (TRIP) and twin induced plasticity (TWIP) aided steels as well as high Mn-N alloyed stainless steels.
AB - Nitrogen solubility in Fe-Mn melts was measured using a N 2 bubbling and sampling method at temperatures from 1823 K to 1923 K (1550 °C to 1650 °C) for manganese content to about 25 mass pct. The effect of temperature on the nitrogen solubility was well described based on the thermodynamic behavior of Fe-Mn system. Furthermore, the interaction parameter between Mn and N was evaluated as a function of temperature. The present results can be used in thermodynamic analyses of the formation of nitride compounds such as AlN or TiN in high manganese steel melts for example, transformation induced plasticity (TRIP) and twin induced plasticity (TWIP) aided steels as well as high Mn-N alloyed stainless steels.
UR - http://www.scopus.com/inward/record.url?scp=84857030056&partnerID=8YFLogxK
UR - http://www.scopus.com/inward/citedby.url?scp=84857030056&partnerID=8YFLogxK
U2 - 10.1007/s11663-011-9582-6
DO - 10.1007/s11663-011-9582-6
M3 - Article
AN - SCOPUS:84857030056
VL - 42
SP - 1081
EP - 1085
JO - Metallurgical and Materials Transactions B: Process Metallurgy and Materials Processing Science
JF - Metallurgical and Materials Transactions B: Process Metallurgy and Materials Processing Science
SN - 1073-5615
IS - 6
ER -