Development of electrodeposited IrO2 electrodes as anodes in polymer electrolyte membrane water electrolysis

Byung Seok Lee, Sang Hyun Ahn, Hee Young Park, Insoo Choi, Sung Jong Yoo, Hyoung Juhn Kim, Dirk Henkensmeier, Jin Young Kim, Sehkyu Park, Suk Woo Nam, Kwan Young Lee, Jong Hyun Jang

Research output: Contribution to journalArticlepeer-review

79 Citations (Scopus)


To reduce the use of noble metals, iridium oxide (IrO2) catalysts are prepared on carbon paper (CP) by electrodeposition for use as the anodes in polymer electrolyte membrane water electrolysis (PEMWE). The activities of the fabricated electrodes toward the oxygen evolution reaction are evaluated. The loading amount and morphology of the IrO2 deposits are varied by controlling the electrodeposition potential (Edep) and time (tdep). When electrodeposited at 0.7V, the IrO2 loading ranges from 0.007 to 0.464mgcm-2 (tdep: 1~30min). In the PEMWE test at 90°C, the IrO2/CP electrode with an IrO2 loading of 0.1mgcm-2 shows the highest performance (1.92Acm-2 at 1.8V) in which high IrO2 utilization is achieved without significant exposure of the substrate carbon surface. The developed IrO2/CP electrodes provide cell performances comparable to those in previous reports with a higher IrO2 loading, indicating markedly enhanced mass activity.

Original languageEnglish
Pages (from-to)285-291
Number of pages7
JournalApplied Catalysis B: Environmental
Publication statusPublished - 2015 Dec 1


  • Electrodeposition
  • Iridium oxide
  • Oxygen evolution reaction
  • Polymer electrolyte membrane water electrolysis
  • Single cell test

ASJC Scopus subject areas

  • Catalysis
  • Environmental Science(all)
  • Process Chemistry and Technology


Dive into the research topics of 'Development of electrodeposited IrO<sub>2</sub> electrodes as anodes in polymer electrolyte membrane water electrolysis'. Together they form a unique fingerprint.

Cite this