Dye degradation studies of Mo-doped TiO2 thin films developed by reactive sputtering

M. Sreedhar, J. Brijitta, I. Neelakanta Reddy, Migyung Cho, Jaesool Shim, Parthasarathi Bera, Bhavana N. Joshi, Suk Goo Yoon

Research output: Contribution to journalArticlepeer-review

4 Citations (Scopus)

Abstract

TiO2 thin films with various Mo concentrations have been deposited on glass and n-type silicon (100) substrates by this radio-frequency (RF) reactive magnetron sputtering at 400°C substrate temperature. The crystal structure, surface morphology, composition, and elemental oxidation states of the films have been analyzed by using X-ray diffraction, field emission scanning electron microscopy, atomic force microscopy, and X-ray photoelectron spectroscopy, respectively. Ultraviolet-visible spectroscopy has been used to investigate the degradation, transmittance, and absorption properties of doped and undoped TiO2 films. The photocatalytic degradation activity of the films was evaluated by using methylene blue under a light intensity of 100 mW cm−2. The X-ray diffraction patterns show the presence of anatase phase of TiO2 in the developed films. X-ray photoelectron spectroscopy studies have confirmed that Mo is present only as Mo6+ ions in all films. The Mo/TiO2 band gap decreases from ~3.3 to 3.1 eV with increasing Mo dopant concentrations. Dye degradation of ~60% is observed in Mo/TiO2 samples, which is much higher than that of pure TiO2.

Original languageEnglish
Pages (from-to)171-179
Number of pages9
JournalSurface and Interface Analysis
Volume50
Issue number2
DOIs
Publication statusPublished - 2018 Feb 1

Keywords

  • band gap
  • dye degradation
  • Mo/TiO
  • thin film
  • transmittance

ASJC Scopus subject areas

  • Chemistry(all)
  • Condensed Matter Physics
  • Surfaces and Interfaces
  • Surfaces, Coatings and Films
  • Materials Chemistry

Fingerprint Dive into the research topics of 'Dye degradation studies of Mo-doped TiO<sub>2</sub> thin films developed by reactive sputtering'. Together they form a unique fingerprint.

Cite this