Effects of debinding process on properties of sintered AlN substrate

Shi Yeon Kim, Dong Hun Yeo, Hyo Soon Shin, Bum Sup Kim, Hyuk Chun Kwon, Ho Gyu Yoon

Research output: Contribution to journalArticle

Abstract

We fabricated the AlN substrate using tape casting method and investigated the effect of carbon content on sinterability and thermal conductivity. The carbon residue content was measured after the debinding of the AlN green sheet containing 1 wt% Ca–Al–Si–O glass (CAS glass) in the range of 300–1000°C in atmospheres of air, N2, vacuum, and wet N2. The carbon residue content was 0.21 wt% after debinding in the wet N2 atmosphere at 800°C, 0.59 wt% after debinding at 1000°C in the N2 atmosphere, and 1.1 wt% after debinding in the N2 atmosphere at 700°C. The debinded specimen was sintered at 1850°C for 3 h in the N2 atmosphere. As a result, when the residual carbon content was 0.2 wt%, the bulk density was found to be highest with 3.22 g/cm3, and the thermal conductivity was 93 W/m∙K. When the residual carbon content was 0.59 wt%, the bulk density was almost the same at 3.21 g/cm3, and the thermal conductivity was significantly increased to 161 W/m∙K. When the residual carbon content was 1.1 wt%, the bulk density was 2.71 g/cm3, and the thermal conductivity was 60 W/m∙K, degrading the sintered properties.

Original languageEnglish
JournalCeramics International
DOIs
Publication statusPublished - 2019 Jan 1

Fingerprint

Carbon
Thermal conductivity
Substrates
Tapes
Casting
Vacuum
Glass
Air

Keywords

  • AlN
  • Carbon residue
  • Debinding process
  • Green sheet
  • Tape casting
  • Thermal conductivity

ASJC Scopus subject areas

  • Electronic, Optical and Magnetic Materials
  • Ceramics and Composites
  • Process Chemistry and Technology
  • Surfaces, Coatings and Films
  • Materials Chemistry

Cite this

Effects of debinding process on properties of sintered AlN substrate. / Kim, Shi Yeon; Yeo, Dong Hun; Shin, Hyo Soon; Kim, Bum Sup; Kwon, Hyuk Chun; Yoon, Ho Gyu.

In: Ceramics International, 01.01.2019.

Research output: Contribution to journalArticle

Kim, Shi Yeon ; Yeo, Dong Hun ; Shin, Hyo Soon ; Kim, Bum Sup ; Kwon, Hyuk Chun ; Yoon, Ho Gyu. / Effects of debinding process on properties of sintered AlN substrate. In: Ceramics International. 2019.
@article{9930a64904cc4918b5aaf45438f1f161,
title = "Effects of debinding process on properties of sintered AlN substrate",
abstract = "We fabricated the AlN substrate using tape casting method and investigated the effect of carbon content on sinterability and thermal conductivity. The carbon residue content was measured after the debinding of the AlN green sheet containing 1 wt{\%} Ca–Al–Si–O glass (CAS glass) in the range of 300–1000°C in atmospheres of air, N2, vacuum, and wet N2. The carbon residue content was 0.21 wt{\%} after debinding in the wet N2 atmosphere at 800°C, 0.59 wt{\%} after debinding at 1000°C in the N2 atmosphere, and 1.1 wt{\%} after debinding in the N2 atmosphere at 700°C. The debinded specimen was sintered at 1850°C for 3 h in the N2 atmosphere. As a result, when the residual carbon content was 0.2 wt{\%}, the bulk density was found to be highest with 3.22 g/cm3, and the thermal conductivity was 93 W/m∙K. When the residual carbon content was 0.59 wt{\%}, the bulk density was almost the same at 3.21 g/cm3, and the thermal conductivity was significantly increased to 161 W/m∙K. When the residual carbon content was 1.1 wt{\%}, the bulk density was 2.71 g/cm3, and the thermal conductivity was 60 W/m∙K, degrading the sintered properties.",
keywords = "AlN, Carbon residue, Debinding process, Green sheet, Tape casting, Thermal conductivity",
author = "Kim, {Shi Yeon} and Yeo, {Dong Hun} and Shin, {Hyo Soon} and Kim, {Bum Sup} and Kwon, {Hyuk Chun} and Yoon, {Ho Gyu}",
year = "2019",
month = "1",
day = "1",
doi = "10.1016/j.ceramint.2019.06.010",
language = "English",
journal = "Ceramics International",
issn = "0272-8842",
publisher = "Elsevier Limited",

}

TY - JOUR

T1 - Effects of debinding process on properties of sintered AlN substrate

AU - Kim, Shi Yeon

AU - Yeo, Dong Hun

AU - Shin, Hyo Soon

AU - Kim, Bum Sup

AU - Kwon, Hyuk Chun

AU - Yoon, Ho Gyu

PY - 2019/1/1

Y1 - 2019/1/1

N2 - We fabricated the AlN substrate using tape casting method and investigated the effect of carbon content on sinterability and thermal conductivity. The carbon residue content was measured after the debinding of the AlN green sheet containing 1 wt% Ca–Al–Si–O glass (CAS glass) in the range of 300–1000°C in atmospheres of air, N2, vacuum, and wet N2. The carbon residue content was 0.21 wt% after debinding in the wet N2 atmosphere at 800°C, 0.59 wt% after debinding at 1000°C in the N2 atmosphere, and 1.1 wt% after debinding in the N2 atmosphere at 700°C. The debinded specimen was sintered at 1850°C for 3 h in the N2 atmosphere. As a result, when the residual carbon content was 0.2 wt%, the bulk density was found to be highest with 3.22 g/cm3, and the thermal conductivity was 93 W/m∙K. When the residual carbon content was 0.59 wt%, the bulk density was almost the same at 3.21 g/cm3, and the thermal conductivity was significantly increased to 161 W/m∙K. When the residual carbon content was 1.1 wt%, the bulk density was 2.71 g/cm3, and the thermal conductivity was 60 W/m∙K, degrading the sintered properties.

AB - We fabricated the AlN substrate using tape casting method and investigated the effect of carbon content on sinterability and thermal conductivity. The carbon residue content was measured after the debinding of the AlN green sheet containing 1 wt% Ca–Al–Si–O glass (CAS glass) in the range of 300–1000°C in atmospheres of air, N2, vacuum, and wet N2. The carbon residue content was 0.21 wt% after debinding in the wet N2 atmosphere at 800°C, 0.59 wt% after debinding at 1000°C in the N2 atmosphere, and 1.1 wt% after debinding in the N2 atmosphere at 700°C. The debinded specimen was sintered at 1850°C for 3 h in the N2 atmosphere. As a result, when the residual carbon content was 0.2 wt%, the bulk density was found to be highest with 3.22 g/cm3, and the thermal conductivity was 93 W/m∙K. When the residual carbon content was 0.59 wt%, the bulk density was almost the same at 3.21 g/cm3, and the thermal conductivity was significantly increased to 161 W/m∙K. When the residual carbon content was 1.1 wt%, the bulk density was 2.71 g/cm3, and the thermal conductivity was 60 W/m∙K, degrading the sintered properties.

KW - AlN

KW - Carbon residue

KW - Debinding process

KW - Green sheet

KW - Tape casting

KW - Thermal conductivity

UR - http://www.scopus.com/inward/record.url?scp=85067170128&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=85067170128&partnerID=8YFLogxK

U2 - 10.1016/j.ceramint.2019.06.010

DO - 10.1016/j.ceramint.2019.06.010

M3 - Article

JO - Ceramics International

JF - Ceramics International

SN - 0272-8842

ER -