Electrochemical properties of P2-type Na2/3Ni1/3Mn2/3O2 plates synthesized by spray pyrolysis process for sodium-ion batteries

Seung Yeon Lee, Jong Hwa Kim, Yun Chan Kang

Research output: Contribution to journalArticle

20 Citations (Scopus)

Abstract

P2-type Na2/3Ni1/3Mn2/3O2 plates with homogeneous composition and regular morphology are prepared by spray pyrolysis. The rhombohedral P3-Na2/3Ni1/3Mn2/3O2 microspheres formed by one-pot spray pyrolysis transform into hexagonal P2-Na2/3Ni1/3Mn2/3O2 plates after post-treatment at temperatures between 800 and 1000 °C. The mean size and thickness of P2-Na2/3Ni1/3Mn2/3O2 plates obtained after post-treatment at 900 °C are 2.2 μm and 550 nm, respectively. The initial discharge capacities of P2-Na2/3Ni1/3Mn2/3O2 plates formed at 800, 900, and 1000 °C at a current rate of 0.1C are 69, 86, and 80 mA h g−1, respectively, while the discharge capacities after 200 cycles are 68, 80, and 76 mA h g−1, respectively. However, the discharge capacities of P3-Na2/3Ni1/3Mn2/3O2 powders decrease from 62 to 50 mA h g−1 after 200 cycles. P2-Na2/3Ni1/3Mn2/3O2 plates show low charge-transfer resistance and also exhibit better rate performance than P3-Na2/3Ni1/3Mn2/3O2 powders.

Original languageEnglish
Pages (from-to)86-92
Number of pages7
JournalElectrochimica Acta
Volume225
DOIs
Publication statusPublished - 2017 Jan 20

Fingerprint

Spray pyrolysis
Electrochemical properties
Powders
Sodium
Ions
Microspheres
Charge transfer
Chemical analysis
Temperature

Keywords

  • Cathode material
  • Energy storage materials
  • Sodium-ion batteries
  • Spray pyrolysis

ASJC Scopus subject areas

  • Chemical Engineering(all)
  • Electrochemistry

Cite this

Electrochemical properties of P2-type Na2/3Ni1/3Mn2/3O2 plates synthesized by spray pyrolysis process for sodium-ion batteries. / Lee, Seung Yeon; Kim, Jong Hwa; Kang, Yun Chan.

In: Electrochimica Acta, Vol. 225, 20.01.2017, p. 86-92.

Research output: Contribution to journalArticle

@article{d6d27419c4904c648fe6d236445aefc1,
title = "Electrochemical properties of P2-type Na2/3Ni1/3Mn2/3O2 plates synthesized by spray pyrolysis process for sodium-ion batteries",
abstract = "P2-type Na2/3Ni1/3Mn2/3O2 plates with homogeneous composition and regular morphology are prepared by spray pyrolysis. The rhombohedral P3-Na2/3Ni1/3Mn2/3O2 microspheres formed by one-pot spray pyrolysis transform into hexagonal P2-Na2/3Ni1/3Mn2/3O2 plates after post-treatment at temperatures between 800 and 1000 °C. The mean size and thickness of P2-Na2/3Ni1/3Mn2/3O2 plates obtained after post-treatment at 900 °C are 2.2 μm and 550 nm, respectively. The initial discharge capacities of P2-Na2/3Ni1/3Mn2/3O2 plates formed at 800, 900, and 1000 °C at a current rate of 0.1C are 69, 86, and 80 mA h g−1, respectively, while the discharge capacities after 200 cycles are 68, 80, and 76 mA h g−1, respectively. However, the discharge capacities of P3-Na2/3Ni1/3Mn2/3O2 powders decrease from 62 to 50 mA h g−1 after 200 cycles. P2-Na2/3Ni1/3Mn2/3O2 plates show low charge-transfer resistance and also exhibit better rate performance than P3-Na2/3Ni1/3Mn2/3O2 powders.",
keywords = "Cathode material, Energy storage materials, Sodium-ion batteries, Spray pyrolysis",
author = "Lee, {Seung Yeon} and Kim, {Jong Hwa} and Kang, {Yun Chan}",
year = "2017",
month = "1",
day = "20",
doi = "10.1016/j.electacta.2016.11.141",
language = "English",
volume = "225",
pages = "86--92",
journal = "Electrochimica Acta",
issn = "0013-4686",
publisher = "Elsevier Limited",

}

TY - JOUR

T1 - Electrochemical properties of P2-type Na2/3Ni1/3Mn2/3O2 plates synthesized by spray pyrolysis process for sodium-ion batteries

AU - Lee, Seung Yeon

AU - Kim, Jong Hwa

AU - Kang, Yun Chan

PY - 2017/1/20

Y1 - 2017/1/20

N2 - P2-type Na2/3Ni1/3Mn2/3O2 plates with homogeneous composition and regular morphology are prepared by spray pyrolysis. The rhombohedral P3-Na2/3Ni1/3Mn2/3O2 microspheres formed by one-pot spray pyrolysis transform into hexagonal P2-Na2/3Ni1/3Mn2/3O2 plates after post-treatment at temperatures between 800 and 1000 °C. The mean size and thickness of P2-Na2/3Ni1/3Mn2/3O2 plates obtained after post-treatment at 900 °C are 2.2 μm and 550 nm, respectively. The initial discharge capacities of P2-Na2/3Ni1/3Mn2/3O2 plates formed at 800, 900, and 1000 °C at a current rate of 0.1C are 69, 86, and 80 mA h g−1, respectively, while the discharge capacities after 200 cycles are 68, 80, and 76 mA h g−1, respectively. However, the discharge capacities of P3-Na2/3Ni1/3Mn2/3O2 powders decrease from 62 to 50 mA h g−1 after 200 cycles. P2-Na2/3Ni1/3Mn2/3O2 plates show low charge-transfer resistance and also exhibit better rate performance than P3-Na2/3Ni1/3Mn2/3O2 powders.

AB - P2-type Na2/3Ni1/3Mn2/3O2 plates with homogeneous composition and regular morphology are prepared by spray pyrolysis. The rhombohedral P3-Na2/3Ni1/3Mn2/3O2 microspheres formed by one-pot spray pyrolysis transform into hexagonal P2-Na2/3Ni1/3Mn2/3O2 plates after post-treatment at temperatures between 800 and 1000 °C. The mean size and thickness of P2-Na2/3Ni1/3Mn2/3O2 plates obtained after post-treatment at 900 °C are 2.2 μm and 550 nm, respectively. The initial discharge capacities of P2-Na2/3Ni1/3Mn2/3O2 plates formed at 800, 900, and 1000 °C at a current rate of 0.1C are 69, 86, and 80 mA h g−1, respectively, while the discharge capacities after 200 cycles are 68, 80, and 76 mA h g−1, respectively. However, the discharge capacities of P3-Na2/3Ni1/3Mn2/3O2 powders decrease from 62 to 50 mA h g−1 after 200 cycles. P2-Na2/3Ni1/3Mn2/3O2 plates show low charge-transfer resistance and also exhibit better rate performance than P3-Na2/3Ni1/3Mn2/3O2 powders.

KW - Cathode material

KW - Energy storage materials

KW - Sodium-ion batteries

KW - Spray pyrolysis

UR - http://www.scopus.com/inward/record.url?scp=85007087216&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=85007087216&partnerID=8YFLogxK

U2 - 10.1016/j.electacta.2016.11.141

DO - 10.1016/j.electacta.2016.11.141

M3 - Article

AN - SCOPUS:85007087216

VL - 225

SP - 86

EP - 92

JO - Electrochimica Acta

JF - Electrochimica Acta

SN - 0013-4686

ER -