Fine size (Y,Gd)BO3: Eu phosphor powders prepared from precursor powders with hollow shape and large size

Hye Young Koo, Da Rae Ko, Sang Ho Lee, Su Min Lee, Yun Chan Kang, Jong Heun Lee

Research output: Contribution to journalArticle

6 Citations (Scopus)

Abstract

Fine size (Y,Gd)BO3:Eu phosphor powders with high photoluminescence intensity under vacuum ultraviolet were prepared by spray pyrolysis. The precursor powders with hollow shape and large size were prepared by spray pyrolysis from the spray solution with citric acid. The precursor powders turned to the (Y,Gd)BO3:Eu phosphor powders after post-treatment at temperatures between 900 and 1100 °C. The mean sizes of the phosphor powders post-treated at a temperature of 950 °C were 0.37 μm. The photoluminescence intensity of the fine size (Y,Gd)BO3:Eu phosphor powders was 95% of that of the commercial (Y,Gd)BO3:Eu phosphor powders with micron sizes.

Original languageEnglish
Pages (from-to)260-265
Number of pages6
JournalJournal of Alloys and Compounds
Volume503
Issue number1
DOIs
Publication statusPublished - 2010 Jul 30

Keywords

  • Chemical synthesis
  • Gas-solid reaction

ASJC Scopus subject areas

  • Mechanics of Materials
  • Mechanical Engineering
  • Metals and Alloys
  • Materials Chemistry

Fingerprint Dive into the research topics of 'Fine size (Y,Gd)BO<sub>3</sub>: Eu phosphor powders prepared from precursor powders with hollow shape and large size'. Together they form a unique fingerprint.

  • Cite this