Fracture initiation associated with chemical degradation: Observation and modeling

Byoung-Ho Choi, Zhenwen Zhou, Alexander Chudnovsky, Salvatore S. Stivala, Kalyan Sehanobish, Clive P. Bosnyak

Research output: Contribution to journalArticle

37 Citations (Scopus)

Abstract

The fracture initiation in engineering thermoplastics resulting from chemical degradation is usually observed in the form of a microcrack network within a surface layer of degraded polymer exposed to a combined action of mechanical stresses and chemically aggressive environment. Degradation of polymers is usually manifested in a reduction of molecular weight, increase of crystallinity in semi crystalline polymers, increase of material density, a subtle increase in yield strength, and a dramatic reduction in toughness. An increase in material density, i.e., shrinkage of the degraded layer is constrained by adjacent unchanged material results in a buildup of tensile stress within the degraded layer and compressive stress in the adjacent unchanged material due to increasing incompatibility between the two. These stresses are an addition to preexisting manufacturing and service stresses. At a certain level of degradation, a combination of toughness reduction and increase of tensile stress result in fracture initiation. A quantitative model of the described above processes is presented in these work. For specificity, the internally pressurized plastic pipes that transport a fluid containing a chemically aggressive (oxidizing) agent is used as the model of fracture initiation. Experimental observations of material density and toughness dependence on degradation reported elsewhere are employed in the model. An equation for determination of a critical level of degradation corresponding to the offset of fracture is constructed. The critical level of degradation for fracture initiation depends on the rates of toughness deterioration and build-up of the degradation related stresses as well as on the manufacturing and service stresses. A method for evaluation of the time interval prior to fracture initiation is also formulated.

Original languageEnglish
Pages (from-to)681-695
Number of pages15
JournalInternational Journal of Solids and Structures
Volume42
Issue number2
DOIs
Publication statusPublished - 2005 Jan 1
Externally publishedYes

Fingerprint

Degradation
degradation
Toughness
toughness
Modeling
Polymers
tensile stress
Tensile stress
polymers
Adjacent
manufacturing
Manufacturing
Plastic pipe
Mechanical Stress
incompatibility
Microcracks
microcracks
yield strength
Shrinkage
Observation

Keywords

  • Chemical degradation
  • Fracture initiation
  • Fracture toughness
  • Material density change
  • Microcrack network

ASJC Scopus subject areas

  • Mechanical Engineering
  • Mechanics of Materials

Cite this

Fracture initiation associated with chemical degradation : Observation and modeling. / Choi, Byoung-Ho; Zhou, Zhenwen; Chudnovsky, Alexander; Stivala, Salvatore S.; Sehanobish, Kalyan; Bosnyak, Clive P.

In: International Journal of Solids and Structures, Vol. 42, No. 2, 01.01.2005, p. 681-695.

Research output: Contribution to journalArticle

Choi, Byoung-Ho ; Zhou, Zhenwen ; Chudnovsky, Alexander ; Stivala, Salvatore S. ; Sehanobish, Kalyan ; Bosnyak, Clive P. / Fracture initiation associated with chemical degradation : Observation and modeling. In: International Journal of Solids and Structures. 2005 ; Vol. 42, No. 2. pp. 681-695.
@article{92bc525555534fc2a03254b7767d2938,
title = "Fracture initiation associated with chemical degradation: Observation and modeling",
abstract = "The fracture initiation in engineering thermoplastics resulting from chemical degradation is usually observed in the form of a microcrack network within a surface layer of degraded polymer exposed to a combined action of mechanical stresses and chemically aggressive environment. Degradation of polymers is usually manifested in a reduction of molecular weight, increase of crystallinity in semi crystalline polymers, increase of material density, a subtle increase in yield strength, and a dramatic reduction in toughness. An increase in material density, i.e., shrinkage of the degraded layer is constrained by adjacent unchanged material results in a buildup of tensile stress within the degraded layer and compressive stress in the adjacent unchanged material due to increasing incompatibility between the two. These stresses are an addition to preexisting manufacturing and service stresses. At a certain level of degradation, a combination of toughness reduction and increase of tensile stress result in fracture initiation. A quantitative model of the described above processes is presented in these work. For specificity, the internally pressurized plastic pipes that transport a fluid containing a chemically aggressive (oxidizing) agent is used as the model of fracture initiation. Experimental observations of material density and toughness dependence on degradation reported elsewhere are employed in the model. An equation for determination of a critical level of degradation corresponding to the offset of fracture is constructed. The critical level of degradation for fracture initiation depends on the rates of toughness deterioration and build-up of the degradation related stresses as well as on the manufacturing and service stresses. A method for evaluation of the time interval prior to fracture initiation is also formulated.",
keywords = "Chemical degradation, Fracture initiation, Fracture toughness, Material density change, Microcrack network",
author = "Byoung-Ho Choi and Zhenwen Zhou and Alexander Chudnovsky and Stivala, {Salvatore S.} and Kalyan Sehanobish and Bosnyak, {Clive P.}",
year = "2005",
month = "1",
day = "1",
doi = "10.1016/j.ijsolstr.2004.06.028",
language = "English",
volume = "42",
pages = "681--695",
journal = "International Journal of Solids and Structures",
issn = "0020-7683",
publisher = "Elsevier Limited",
number = "2",

}

TY - JOUR

T1 - Fracture initiation associated with chemical degradation

T2 - Observation and modeling

AU - Choi, Byoung-Ho

AU - Zhou, Zhenwen

AU - Chudnovsky, Alexander

AU - Stivala, Salvatore S.

AU - Sehanobish, Kalyan

AU - Bosnyak, Clive P.

PY - 2005/1/1

Y1 - 2005/1/1

N2 - The fracture initiation in engineering thermoplastics resulting from chemical degradation is usually observed in the form of a microcrack network within a surface layer of degraded polymer exposed to a combined action of mechanical stresses and chemically aggressive environment. Degradation of polymers is usually manifested in a reduction of molecular weight, increase of crystallinity in semi crystalline polymers, increase of material density, a subtle increase in yield strength, and a dramatic reduction in toughness. An increase in material density, i.e., shrinkage of the degraded layer is constrained by adjacent unchanged material results in a buildup of tensile stress within the degraded layer and compressive stress in the adjacent unchanged material due to increasing incompatibility between the two. These stresses are an addition to preexisting manufacturing and service stresses. At a certain level of degradation, a combination of toughness reduction and increase of tensile stress result in fracture initiation. A quantitative model of the described above processes is presented in these work. For specificity, the internally pressurized plastic pipes that transport a fluid containing a chemically aggressive (oxidizing) agent is used as the model of fracture initiation. Experimental observations of material density and toughness dependence on degradation reported elsewhere are employed in the model. An equation for determination of a critical level of degradation corresponding to the offset of fracture is constructed. The critical level of degradation for fracture initiation depends on the rates of toughness deterioration and build-up of the degradation related stresses as well as on the manufacturing and service stresses. A method for evaluation of the time interval prior to fracture initiation is also formulated.

AB - The fracture initiation in engineering thermoplastics resulting from chemical degradation is usually observed in the form of a microcrack network within a surface layer of degraded polymer exposed to a combined action of mechanical stresses and chemically aggressive environment. Degradation of polymers is usually manifested in a reduction of molecular weight, increase of crystallinity in semi crystalline polymers, increase of material density, a subtle increase in yield strength, and a dramatic reduction in toughness. An increase in material density, i.e., shrinkage of the degraded layer is constrained by adjacent unchanged material results in a buildup of tensile stress within the degraded layer and compressive stress in the adjacent unchanged material due to increasing incompatibility between the two. These stresses are an addition to preexisting manufacturing and service stresses. At a certain level of degradation, a combination of toughness reduction and increase of tensile stress result in fracture initiation. A quantitative model of the described above processes is presented in these work. For specificity, the internally pressurized plastic pipes that transport a fluid containing a chemically aggressive (oxidizing) agent is used as the model of fracture initiation. Experimental observations of material density and toughness dependence on degradation reported elsewhere are employed in the model. An equation for determination of a critical level of degradation corresponding to the offset of fracture is constructed. The critical level of degradation for fracture initiation depends on the rates of toughness deterioration and build-up of the degradation related stresses as well as on the manufacturing and service stresses. A method for evaluation of the time interval prior to fracture initiation is also formulated.

KW - Chemical degradation

KW - Fracture initiation

KW - Fracture toughness

KW - Material density change

KW - Microcrack network

UR - http://www.scopus.com/inward/record.url?scp=7444266889&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=7444266889&partnerID=8YFLogxK

U2 - 10.1016/j.ijsolstr.2004.06.028

DO - 10.1016/j.ijsolstr.2004.06.028

M3 - Article

AN - SCOPUS:7444266889

VL - 42

SP - 681

EP - 695

JO - International Journal of Solids and Structures

JF - International Journal of Solids and Structures

SN - 0020-7683

IS - 2

ER -