Hysteresis-less inverted CH3NH3PbI3 planar perovskite hybrid solar cells with 18.1% power conversion efficiency

Jin Hyuck Heo, Hye Ji Han, Dasom Kim, Tae Kyu Ahn, Sang Hyuk Im

Research output: Contribution to journalArticle

747 Citations (Scopus)

Abstract

Hysteresis-less inverted ITO/PEDOT:PSS/CH3NH3PbI3 (MAPbI3)/PCBM/Au planar hybrid solar cells with 18.1% average power conversion efficiency irrespective of the scan rate were fabricated by depositing dense pinhole-free MAPbI3 perovskite on a PEDOT:PSS/ITO substrate via a single-step spin-coating of solubility controlled MAPbI3 solution. The conductivities of PEDOT:PSS, PCBM, poly(triaryl amine) (PTAA):tert-butylpyrridne (tBP) + Li-bis(trifluoromethanesulfonyl)imide (Li-TFSI), MAPbI3, and TiO2 were 0.014, 0.016, 0.034, 0.015, and 0.00006 mS cm-1, respectively. The average PL lifetimes (τav) of the inverted and normal cell were 1.277 and 1.94 ns, respectively. The diffusion coefficient (Dn) and charge carrier lifetime (τn) for the inverted MAPbI3 planar hybrid solar cells were increased by 1.14-fold and 1.1-fold, respectively, compared with the conventional FTO/TiO2/MAPbI3/PTAA:tBP + Li-TFSI/Au planar hybrid cells. Hence, the inverted MAPbI3 planar hybrid solar cells exhibited better power conversion efficiency and stability than the conventional MAPbI3 cells because (i) the electron extraction from MAPbI3 to the electron conductor was improved because the electron conductivity of PCBM is higher than that of TiO2; (ii) the EQE value was increased by the better charge injection/separation efficiency between MAPbI3 and PCBM, and by the higher charge collection efficiency than the conventional cell; (iii) the fill factor is improved by the increased Dn and τn; and (iv) the air and humidity stability is improved by the absence of corrosive additives in the device architecture and the hydrophobicity of the PCBM top layer. The reduced current density-voltage (J-V) hysteresis with respect to the scan rate and scan direction in the inverted planar hybrid solar cells could be attributed to a more balanced electron flux (Je) and hole flux (Jh), and a reduced number of surface traps.

Original languageEnglish
Pages (from-to)1602-1608
Number of pages7
JournalEnergy and Environmental Science
Volume8
Issue number5
DOIs
Publication statusPublished - 2015 May 1
Externally publishedYes

Fingerprint

perovskite
hysteresis
Perovskite
Conversion efficiency
Hysteresis
Solar cells
Electrons
electron
Amines
Fluxes
conductivity
Caustics
Charge injection
Carrier lifetime
Spin coating
fold
Hydrophobicity
Charge carriers
hydrophobicity
Atmospheric humidity

ASJC Scopus subject areas

  • Environmental Chemistry
  • Renewable Energy, Sustainability and the Environment
  • Nuclear Energy and Engineering
  • Pollution

Cite this

Hysteresis-less inverted CH3NH3PbI3 planar perovskite hybrid solar cells with 18.1% power conversion efficiency. / Heo, Jin Hyuck; Han, Hye Ji; Kim, Dasom; Ahn, Tae Kyu; Im, Sang Hyuk.

In: Energy and Environmental Science, Vol. 8, No. 5, 01.05.2015, p. 1602-1608.

Research output: Contribution to journalArticle

@article{822011907e0944b7b8d96f52a94c6210,
title = "Hysteresis-less inverted CH3NH3PbI3 planar perovskite hybrid solar cells with 18.1{\%} power conversion efficiency",
abstract = "Hysteresis-less inverted ITO/PEDOT:PSS/CH3NH3PbI3 (MAPbI3)/PCBM/Au planar hybrid solar cells with 18.1{\%} average power conversion efficiency irrespective of the scan rate were fabricated by depositing dense pinhole-free MAPbI3 perovskite on a PEDOT:PSS/ITO substrate via a single-step spin-coating of solubility controlled MAPbI3 solution. The conductivities of PEDOT:PSS, PCBM, poly(triaryl amine) (PTAA):tert-butylpyrridne (tBP) + Li-bis(trifluoromethanesulfonyl)imide (Li-TFSI), MAPbI3, and TiO2 were 0.014, 0.016, 0.034, 0.015, and 0.00006 mS cm-1, respectively. The average PL lifetimes (τav) of the inverted and normal cell were 1.277 and 1.94 ns, respectively. The diffusion coefficient (Dn) and charge carrier lifetime (τn) for the inverted MAPbI3 planar hybrid solar cells were increased by 1.14-fold and 1.1-fold, respectively, compared with the conventional FTO/TiO2/MAPbI3/PTAA:tBP + Li-TFSI/Au planar hybrid cells. Hence, the inverted MAPbI3 planar hybrid solar cells exhibited better power conversion efficiency and stability than the conventional MAPbI3 cells because (i) the electron extraction from MAPbI3 to the electron conductor was improved because the electron conductivity of PCBM is higher than that of TiO2; (ii) the EQE value was increased by the better charge injection/separation efficiency between MAPbI3 and PCBM, and by the higher charge collection efficiency than the conventional cell; (iii) the fill factor is improved by the increased Dn and τn; and (iv) the air and humidity stability is improved by the absence of corrosive additives in the device architecture and the hydrophobicity of the PCBM top layer. The reduced current density-voltage (J-V) hysteresis with respect to the scan rate and scan direction in the inverted planar hybrid solar cells could be attributed to a more balanced electron flux (Je) and hole flux (Jh), and a reduced number of surface traps.",
author = "Heo, {Jin Hyuck} and Han, {Hye Ji} and Dasom Kim and Ahn, {Tae Kyu} and Im, {Sang Hyuk}",
year = "2015",
month = "5",
day = "1",
doi = "10.1039/c5ee00120j",
language = "English",
volume = "8",
pages = "1602--1608",
journal = "Energy and Environmental Science",
issn = "1754-5692",
publisher = "Royal Society of Chemistry",
number = "5",

}

TY - JOUR

T1 - Hysteresis-less inverted CH3NH3PbI3 planar perovskite hybrid solar cells with 18.1% power conversion efficiency

AU - Heo, Jin Hyuck

AU - Han, Hye Ji

AU - Kim, Dasom

AU - Ahn, Tae Kyu

AU - Im, Sang Hyuk

PY - 2015/5/1

Y1 - 2015/5/1

N2 - Hysteresis-less inverted ITO/PEDOT:PSS/CH3NH3PbI3 (MAPbI3)/PCBM/Au planar hybrid solar cells with 18.1% average power conversion efficiency irrespective of the scan rate were fabricated by depositing dense pinhole-free MAPbI3 perovskite on a PEDOT:PSS/ITO substrate via a single-step spin-coating of solubility controlled MAPbI3 solution. The conductivities of PEDOT:PSS, PCBM, poly(triaryl amine) (PTAA):tert-butylpyrridne (tBP) + Li-bis(trifluoromethanesulfonyl)imide (Li-TFSI), MAPbI3, and TiO2 were 0.014, 0.016, 0.034, 0.015, and 0.00006 mS cm-1, respectively. The average PL lifetimes (τav) of the inverted and normal cell were 1.277 and 1.94 ns, respectively. The diffusion coefficient (Dn) and charge carrier lifetime (τn) for the inverted MAPbI3 planar hybrid solar cells were increased by 1.14-fold and 1.1-fold, respectively, compared with the conventional FTO/TiO2/MAPbI3/PTAA:tBP + Li-TFSI/Au planar hybrid cells. Hence, the inverted MAPbI3 planar hybrid solar cells exhibited better power conversion efficiency and stability than the conventional MAPbI3 cells because (i) the electron extraction from MAPbI3 to the electron conductor was improved because the electron conductivity of PCBM is higher than that of TiO2; (ii) the EQE value was increased by the better charge injection/separation efficiency between MAPbI3 and PCBM, and by the higher charge collection efficiency than the conventional cell; (iii) the fill factor is improved by the increased Dn and τn; and (iv) the air and humidity stability is improved by the absence of corrosive additives in the device architecture and the hydrophobicity of the PCBM top layer. The reduced current density-voltage (J-V) hysteresis with respect to the scan rate and scan direction in the inverted planar hybrid solar cells could be attributed to a more balanced electron flux (Je) and hole flux (Jh), and a reduced number of surface traps.

AB - Hysteresis-less inverted ITO/PEDOT:PSS/CH3NH3PbI3 (MAPbI3)/PCBM/Au planar hybrid solar cells with 18.1% average power conversion efficiency irrespective of the scan rate were fabricated by depositing dense pinhole-free MAPbI3 perovskite on a PEDOT:PSS/ITO substrate via a single-step spin-coating of solubility controlled MAPbI3 solution. The conductivities of PEDOT:PSS, PCBM, poly(triaryl amine) (PTAA):tert-butylpyrridne (tBP) + Li-bis(trifluoromethanesulfonyl)imide (Li-TFSI), MAPbI3, and TiO2 were 0.014, 0.016, 0.034, 0.015, and 0.00006 mS cm-1, respectively. The average PL lifetimes (τav) of the inverted and normal cell were 1.277 and 1.94 ns, respectively. The diffusion coefficient (Dn) and charge carrier lifetime (τn) for the inverted MAPbI3 planar hybrid solar cells were increased by 1.14-fold and 1.1-fold, respectively, compared with the conventional FTO/TiO2/MAPbI3/PTAA:tBP + Li-TFSI/Au planar hybrid cells. Hence, the inverted MAPbI3 planar hybrid solar cells exhibited better power conversion efficiency and stability than the conventional MAPbI3 cells because (i) the electron extraction from MAPbI3 to the electron conductor was improved because the electron conductivity of PCBM is higher than that of TiO2; (ii) the EQE value was increased by the better charge injection/separation efficiency between MAPbI3 and PCBM, and by the higher charge collection efficiency than the conventional cell; (iii) the fill factor is improved by the increased Dn and τn; and (iv) the air and humidity stability is improved by the absence of corrosive additives in the device architecture and the hydrophobicity of the PCBM top layer. The reduced current density-voltage (J-V) hysteresis with respect to the scan rate and scan direction in the inverted planar hybrid solar cells could be attributed to a more balanced electron flux (Je) and hole flux (Jh), and a reduced number of surface traps.

UR - http://www.scopus.com/inward/record.url?scp=84928952050&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=84928952050&partnerID=8YFLogxK

U2 - 10.1039/c5ee00120j

DO - 10.1039/c5ee00120j

M3 - Article

AN - SCOPUS:84928952050

VL - 8

SP - 1602

EP - 1608

JO - Energy and Environmental Science

JF - Energy and Environmental Science

SN - 1754-5692

IS - 5

ER -