Magnetic and microstructural characteristics of Nd-Fe-B sintered magnets doped with Dy2O3 and DyF3 powders

Song E. Park, Tae Hoon Kim, Seong Rae Lee, Dong Hwan Kim, Seok Nam-Kung, Tae Suk Jang

Research output: Contribution to journalArticle

22 Citations (Scopus)

Abstract

Magnetic and microstructural properties of (Nd26.06, Dy 6.51)-Febal.-B0.97-M2.39 (wt.%) (M = Cu, Al, Co, and Nb) sintered magnets doped with Dy2 O3 and DyF3 powders were studied. In the case of the Dy 2O3-doped magnet, Dy was distributed along the near grain boundaries. In contrast, the DyF3-doped magnet and the undoped magnet showed that Dy was distributed uniformly in the main phase. The coercivity and the remanence of the Dy2 O3 and DyF3 -doped magnets were 33.2 kOe, 11.64 kG, and 34.5 kOe, 11.21 kG, respectively. The coercivity of the DyF3-doped magnet was the largest but its remanence was the smallest among other magnets because the Dy was distributed throughout the main phase. Uniform distribution of the Dy in the DyF3-doped magnet was probably due to their lower bonding energy and higher chemical potential for diffusion.

Original languageEnglish
Article number6027997
Pages (from-to)3259-3262
Number of pages4
JournalIEEE Transactions on Magnetics
Volume47
Issue number10
DOIs
Publication statusPublished - 2011 Oct 1

Fingerprint

Powders
Magnets
Remanence
Coercive force
Chemical potential
Grain boundaries

Keywords

  • DyO
  • DyF doping
  • magnetic property
  • microstructure
  • Nd-Fe-B sintered magnets

ASJC Scopus subject areas

  • Electrical and Electronic Engineering
  • Electronic, Optical and Magnetic Materials

Cite this

Magnetic and microstructural characteristics of Nd-Fe-B sintered magnets doped with Dy2O3 and DyF3 powders. / Park, Song E.; Kim, Tae Hoon; Lee, Seong Rae; Kim, Dong Hwan; Nam-Kung, Seok; Jang, Tae Suk.

In: IEEE Transactions on Magnetics, Vol. 47, No. 10, 6027997, 01.10.2011, p. 3259-3262.

Research output: Contribution to journalArticle

Park, Song E. ; Kim, Tae Hoon ; Lee, Seong Rae ; Kim, Dong Hwan ; Nam-Kung, Seok ; Jang, Tae Suk. / Magnetic and microstructural characteristics of Nd-Fe-B sintered magnets doped with Dy2O3 and DyF3 powders. In: IEEE Transactions on Magnetics. 2011 ; Vol. 47, No. 10. pp. 3259-3262.
@article{baaf519c019d432e873f35dd72a1622c,
title = "Magnetic and microstructural characteristics of Nd-Fe-B sintered magnets doped with Dy2O3 and DyF3 powders",
abstract = "Magnetic and microstructural properties of (Nd26.06, Dy 6.51)-Febal.-B0.97-M2.39 (wt.{\%}) (M = Cu, Al, Co, and Nb) sintered magnets doped with Dy2 O3 and DyF3 powders were studied. In the case of the Dy 2O3-doped magnet, Dy was distributed along the near grain boundaries. In contrast, the DyF3-doped magnet and the undoped magnet showed that Dy was distributed uniformly in the main phase. The coercivity and the remanence of the Dy2 O3 and DyF3 -doped magnets were 33.2 kOe, 11.64 kG, and 34.5 kOe, 11.21 kG, respectively. The coercivity of the DyF3-doped magnet was the largest but its remanence was the smallest among other magnets because the Dy was distributed throughout the main phase. Uniform distribution of the Dy in the DyF3-doped magnet was probably due to their lower bonding energy and higher chemical potential for diffusion.",
keywords = "DyO, DyF doping, magnetic property, microstructure, Nd-Fe-B sintered magnets",
author = "Park, {Song E.} and Kim, {Tae Hoon} and Lee, {Seong Rae} and Kim, {Dong Hwan} and Seok Nam-Kung and Jang, {Tae Suk}",
year = "2011",
month = "10",
day = "1",
doi = "10.1109/TMAG.2011.2153833",
language = "English",
volume = "47",
pages = "3259--3262",
journal = "IEEE Transactions on Magnetics",
issn = "0018-9464",
publisher = "Institute of Electrical and Electronics Engineers Inc.",
number = "10",

}

TY - JOUR

T1 - Magnetic and microstructural characteristics of Nd-Fe-B sintered magnets doped with Dy2O3 and DyF3 powders

AU - Park, Song E.

AU - Kim, Tae Hoon

AU - Lee, Seong Rae

AU - Kim, Dong Hwan

AU - Nam-Kung, Seok

AU - Jang, Tae Suk

PY - 2011/10/1

Y1 - 2011/10/1

N2 - Magnetic and microstructural properties of (Nd26.06, Dy 6.51)-Febal.-B0.97-M2.39 (wt.%) (M = Cu, Al, Co, and Nb) sintered magnets doped with Dy2 O3 and DyF3 powders were studied. In the case of the Dy 2O3-doped magnet, Dy was distributed along the near grain boundaries. In contrast, the DyF3-doped magnet and the undoped magnet showed that Dy was distributed uniformly in the main phase. The coercivity and the remanence of the Dy2 O3 and DyF3 -doped magnets were 33.2 kOe, 11.64 kG, and 34.5 kOe, 11.21 kG, respectively. The coercivity of the DyF3-doped magnet was the largest but its remanence was the smallest among other magnets because the Dy was distributed throughout the main phase. Uniform distribution of the Dy in the DyF3-doped magnet was probably due to their lower bonding energy and higher chemical potential for diffusion.

AB - Magnetic and microstructural properties of (Nd26.06, Dy 6.51)-Febal.-B0.97-M2.39 (wt.%) (M = Cu, Al, Co, and Nb) sintered magnets doped with Dy2 O3 and DyF3 powders were studied. In the case of the Dy 2O3-doped magnet, Dy was distributed along the near grain boundaries. In contrast, the DyF3-doped magnet and the undoped magnet showed that Dy was distributed uniformly in the main phase. The coercivity and the remanence of the Dy2 O3 and DyF3 -doped magnets were 33.2 kOe, 11.64 kG, and 34.5 kOe, 11.21 kG, respectively. The coercivity of the DyF3-doped magnet was the largest but its remanence was the smallest among other magnets because the Dy was distributed throughout the main phase. Uniform distribution of the Dy in the DyF3-doped magnet was probably due to their lower bonding energy and higher chemical potential for diffusion.

KW - DyO

KW - DyF doping

KW - magnetic property

KW - microstructure

KW - Nd-Fe-B sintered magnets

UR - http://www.scopus.com/inward/record.url?scp=80053490200&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=80053490200&partnerID=8YFLogxK

U2 - 10.1109/TMAG.2011.2153833

DO - 10.1109/TMAG.2011.2153833

M3 - Article

AN - SCOPUS:80053490200

VL - 47

SP - 3259

EP - 3262

JO - IEEE Transactions on Magnetics

JF - IEEE Transactions on Magnetics

SN - 0018-9464

IS - 10

M1 - 6027997

ER -