Microstructural characterization of the emulsified Cu47Ti33Zr11Ni6Sn2Si1 alloy powder

Ho Suk Kang, Hee Sam Kang, Wooyoung Yoon

Research output: Contribution to journalArticle

Abstract

Phase selection and microstructural morphology change of the Cu47Ti33Zr11Ni6Sn2Si1 alloy were investigated through the droplet emulsion technique(DET). The emulsified Cu47Ti33Zr11Ni6Sn2Si1 alloy powders showed several different microstructures depending on the amount of undercooling. The amount of undercooling of the powders was monitored by differential thermal analysis and was matched with the microstructures. The phase transition of Cu47Ti33Zr11Ni6Sn2Si1 alloy powders according to the increase of undercooling proceeds by the process Cu4Ti3 +CuTi +Cu2Ti +Cu51Zr14 → Cu4Ti3 + CuTi + Cu2Ti + Cu51Zr14 + CuTi2 → Cu2Ti + Cu51Zr14 + CuTi2 → Cu51Zr14 +CuTi2. Specifically, the morphology and scale of the CuTi2 phase were examined by SEM observation, and area fraction measurement using an image analyzer, transmission electron microscopy studies, and microhardness tests showed that the amorphous phase could be synthesized by DET. A microstructure selection map of Cu47Ti33Zr11Ni6Sn2Si1 alloy powders for tailored solidification was also suggested.

Original languageEnglish
Pages (from-to)623-634
Number of pages12
JournalSolid State Phenomena
Volume118
DOIs
Publication statusPublished - 2006

    Fingerprint

Keywords

  • Cu-ti-zr-ni-sn-si
  • Droplet emulsion technique(det)
  • Microstructure selection map

ASJC Scopus subject areas

  • Materials Science(all)
  • Condensed Matter Physics
  • Atomic and Molecular Physics, and Optics

Cite this