Microstructure and dielectric properties of the Ti-rich BaO-TiO2 thin films for microwave devices

Bo Yun Jang, Young Hun Jeong, Suk Jin Lee, Kyong Jae Lee, Sahn Nahm, Ho Jung Sun, Hwack Joo Lee

Research output: Contribution to journalArticle

5 Citations (Scopus)

Abstract

Ti-rich BaO-TiO2 thin films were grown on a Pt/Ti/SiO2/Si substrate using rf sputtering and the structural and dielectric properties of the films were investigated. For the film grown at room temperature and rapidly thermal annealed (RTA) at 900 °C for 3 min, an amorphous phase with a small BaTi5 O13 crystalline phase was formed. As the growth temperature increased, the amount of the BaTi5O11 crystalline phase increased. For the film grown at 350 °C and RTA at 900 °C for 3 min, the homogeneous BaTi5O11 phase was formed. The BaTi4O9 phase was developed when the growth temperature exceeded 450 °C. The thin film with the homogeneous BaTi4O9 phase was obtained when the film was grown at 550 °C and RTA at 900 °C for 3 min. The dielectric properties of the films were measured at 1-6 GHz range. The dielectric constant (εr) of the BaTi5 O11 film was about 33 and the dissipation factor was about 0.01. The εr and the dissipation factor of the BaTi4O9 film were about 37 and 0.005, respectively.

Original languageEnglish
Pages (from-to)1913-1916
Number of pages4
JournalJournal of the European Ceramic Society
Volume26
Issue number10-11
DOIs
Publication statusPublished - 2006

Keywords

  • Capacitors
  • Dielectric properties
  • Films
  • Microstructure
  • Ti-rich BaO-TiO

ASJC Scopus subject areas

  • Ceramics and Composites
  • Materials Chemistry

Fingerprint Dive into the research topics of 'Microstructure and dielectric properties of the Ti-rich BaO-TiO<sub>2</sub> thin films for microwave devices'. Together they form a unique fingerprint.

  • Cite this