Microwave dielectric properties of Ca[(Li1/3Nb 2/3)1-x Tix]O3-δ ceramics with glass

Jong Yoon Ha, Ji Won Choi, Chong-Yun Kang, Seok Jin Yoon, Doo Jin Choi, Hyun Jai Kim

Research output: Contribution to journalArticle

8 Citations (Scopus)

Abstract

The effect of the addition of glass on the densification, low temperature sintering, and microwave dielectric properties of the Ca[(Li 1/3Nb2/3)1-x Tix]O 3-δ(CLNT) was investigated. Addition of glass (B 2O3-ZnO-SiO2-PbO system) improved the densification and reduced the sintering temperature from 1150°C to 900°C of Ca[(Li1/3Nb2/3)1-x -Tix]O 3-δ microwave dielectric ceramics. As increasing glass contents from 10 wt% to 15 wt%, the dielectric constants (εr) and bulk density were increased. The quality factor (Q•f0), however, was decreased slightly. The temperature coefficients of the resonant frequency (τf) shifted positive value as increasing glass contents over Ti content is 0.2 mol. The dielectric properties of Ca[(Li1/3Nb 2/3)0.75Ti0.25]O3-δ with 10 wt% glass sintered at 900°C for 3 h were εr = 40 Q•f0 = 11500 GHz, τf = 8, ppm/°C. The relationship between the microstructure and dielectric properties of ceramics was studied by X-ray diffraction (XRD), and scanning electron microscope (SEM).

Original languageEnglish
Pages (from-to)399-403
Number of pages5
JournalJournal of Electroceramics
Volume17
Issue number2-4
DOIs
Publication statusPublished - 2006 Dec 1

Fingerprint

Dielectric properties
dielectric properties
Microwaves
ceramics
microwaves
Glass
glass
densification
Densification
sintering
Sintering
Temperature
resonant frequencies
Q factors
Natural frequencies
Permittivity
Electron microscopes
electron microscopes
permittivity
Scanning

Keywords

  • Addition of glass
  • Dielectric
  • LTCC
  • Microwave

ASJC Scopus subject areas

  • Ceramics and Composites

Cite this

Ha, J. Y., Choi, J. W., Kang, C-Y., Yoon, S. J., Choi, D. J., & Kim, H. J. (2006). Microwave dielectric properties of Ca[(Li1/3Nb 2/3)1-x Tix]O3-δ ceramics with glass. Journal of Electroceramics, 17(2-4), 399-403. https://doi.org/10.1007/s10832-006-9638-1

Microwave dielectric properties of Ca[(Li1/3Nb 2/3)1-x Tix]O3-δ ceramics with glass. / Ha, Jong Yoon; Choi, Ji Won; Kang, Chong-Yun; Yoon, Seok Jin; Choi, Doo Jin; Kim, Hyun Jai.

In: Journal of Electroceramics, Vol. 17, No. 2-4, 01.12.2006, p. 399-403.

Research output: Contribution to journalArticle

Ha, JY, Choi, JW, Kang, C-Y, Yoon, SJ, Choi, DJ & Kim, HJ 2006, 'Microwave dielectric properties of Ca[(Li1/3Nb 2/3)1-x Tix]O3-δ ceramics with glass', Journal of Electroceramics, vol. 17, no. 2-4, pp. 399-403. https://doi.org/10.1007/s10832-006-9638-1
Ha, Jong Yoon ; Choi, Ji Won ; Kang, Chong-Yun ; Yoon, Seok Jin ; Choi, Doo Jin ; Kim, Hyun Jai. / Microwave dielectric properties of Ca[(Li1/3Nb 2/3)1-x Tix]O3-δ ceramics with glass. In: Journal of Electroceramics. 2006 ; Vol. 17, No. 2-4. pp. 399-403.
@article{b9f8e3e1ec534edcb76b4cec3c9e5dd6,
title = "Microwave dielectric properties of Ca[(Li1/3Nb 2/3)1-x Tix]O3-δ ceramics with glass",
abstract = "The effect of the addition of glass on the densification, low temperature sintering, and microwave dielectric properties of the Ca[(Li 1/3Nb2/3)1-x Tix]O 3-δ(CLNT) was investigated. Addition of glass (B 2O3-ZnO-SiO2-PbO system) improved the densification and reduced the sintering temperature from 1150°C to 900°C of Ca[(Li1/3Nb2/3)1-x -Tix]O 3-δ microwave dielectric ceramics. As increasing glass contents from 10 wt{\%} to 15 wt{\%}, the dielectric constants (εr) and bulk density were increased. The quality factor (Q•f0), however, was decreased slightly. The temperature coefficients of the resonant frequency (τf) shifted positive value as increasing glass contents over Ti content is 0.2 mol. The dielectric properties of Ca[(Li1/3Nb 2/3)0.75Ti0.25]O3-δ with 10 wt{\%} glass sintered at 900°C for 3 h were εr = 40 Q•f0 = 11500 GHz, τf = 8, ppm/°C. The relationship between the microstructure and dielectric properties of ceramics was studied by X-ray diffraction (XRD), and scanning electron microscope (SEM).",
keywords = "Addition of glass, Dielectric, LTCC, Microwave",
author = "Ha, {Jong Yoon} and Choi, {Ji Won} and Chong-Yun Kang and Yoon, {Seok Jin} and Choi, {Doo Jin} and Kim, {Hyun Jai}",
year = "2006",
month = "12",
day = "1",
doi = "10.1007/s10832-006-9638-1",
language = "English",
volume = "17",
pages = "399--403",
journal = "Journal of Electroceramics",
issn = "1385-3449",
publisher = "Springer Netherlands",
number = "2-4",

}

TY - JOUR

T1 - Microwave dielectric properties of Ca[(Li1/3Nb 2/3)1-x Tix]O3-δ ceramics with glass

AU - Ha, Jong Yoon

AU - Choi, Ji Won

AU - Kang, Chong-Yun

AU - Yoon, Seok Jin

AU - Choi, Doo Jin

AU - Kim, Hyun Jai

PY - 2006/12/1

Y1 - 2006/12/1

N2 - The effect of the addition of glass on the densification, low temperature sintering, and microwave dielectric properties of the Ca[(Li 1/3Nb2/3)1-x Tix]O 3-δ(CLNT) was investigated. Addition of glass (B 2O3-ZnO-SiO2-PbO system) improved the densification and reduced the sintering temperature from 1150°C to 900°C of Ca[(Li1/3Nb2/3)1-x -Tix]O 3-δ microwave dielectric ceramics. As increasing glass contents from 10 wt% to 15 wt%, the dielectric constants (εr) and bulk density were increased. The quality factor (Q•f0), however, was decreased slightly. The temperature coefficients of the resonant frequency (τf) shifted positive value as increasing glass contents over Ti content is 0.2 mol. The dielectric properties of Ca[(Li1/3Nb 2/3)0.75Ti0.25]O3-δ with 10 wt% glass sintered at 900°C for 3 h were εr = 40 Q•f0 = 11500 GHz, τf = 8, ppm/°C. The relationship between the microstructure and dielectric properties of ceramics was studied by X-ray diffraction (XRD), and scanning electron microscope (SEM).

AB - The effect of the addition of glass on the densification, low temperature sintering, and microwave dielectric properties of the Ca[(Li 1/3Nb2/3)1-x Tix]O 3-δ(CLNT) was investigated. Addition of glass (B 2O3-ZnO-SiO2-PbO system) improved the densification and reduced the sintering temperature from 1150°C to 900°C of Ca[(Li1/3Nb2/3)1-x -Tix]O 3-δ microwave dielectric ceramics. As increasing glass contents from 10 wt% to 15 wt%, the dielectric constants (εr) and bulk density were increased. The quality factor (Q•f0), however, was decreased slightly. The temperature coefficients of the resonant frequency (τf) shifted positive value as increasing glass contents over Ti content is 0.2 mol. The dielectric properties of Ca[(Li1/3Nb 2/3)0.75Ti0.25]O3-δ with 10 wt% glass sintered at 900°C for 3 h were εr = 40 Q•f0 = 11500 GHz, τf = 8, ppm/°C. The relationship between the microstructure and dielectric properties of ceramics was studied by X-ray diffraction (XRD), and scanning electron microscope (SEM).

KW - Addition of glass

KW - Dielectric

KW - LTCC

KW - Microwave

UR - http://www.scopus.com/inward/record.url?scp=33847175249&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=33847175249&partnerID=8YFLogxK

U2 - 10.1007/s10832-006-9638-1

DO - 10.1007/s10832-006-9638-1

M3 - Article

VL - 17

SP - 399

EP - 403

JO - Journal of Electroceramics

JF - Journal of Electroceramics

SN - 1385-3449

IS - 2-4

ER -