One-step approach for nano-crystalline hydroxyapatite coating on titanium via micro-arc oxidation

Min Seok Kim, Jae Jun Ryu, Yun Mo Sung

Research output: Contribution to journalArticle

101 Citations (Scopus)

Abstract

Nano-crystalline hydroxyapatite (HAp) films were formed at the surface of Ti by a single-step micro-arc oxidation (MAO) using Ca2+ and P5+ ion-containing electrolytes. The HAp films were 10-25 μm thick, showing strong crystallinity dependence on the CaCl2 concentration in the electrolytes. Also, the formation of an amorphous CaTiO3 interlayer was identified to exist between the HAp and Ti substrates. In contrast to the previous researches using K2HPO4 for the electrolytes, KH2PO4 was used in this study, and this could allow the formation of the crystalline HAp layer. It is suggested as the most probable mechanism for the HAp formation that the high-density hydroxyl groups of TiO(OH)2, formed by the reactions between the amorphous CaTiO3 interlayer and the H+ ions from the dissolution of the KH2PO4, can play a key role in the nucleation and crystal growth of HAp by attracting Ca2+ and P5+ ions in the electrolytes.

Original languageEnglish
Pages (from-to)1886-1891
Number of pages6
JournalElectrochemistry Communications
Volume9
Issue number8
DOIs
Publication statusPublished - 2007 Aug 1

    Fingerprint

Keywords

  • Coating
  • Electrolytes
  • Hydroxyapatite (HAp)
  • Micro-arc oxidation (MAO)
  • Nanocrystals

ASJC Scopus subject areas

  • Chemical Engineering(all)
  • Analytical Chemistry
  • Electrochemistry

Cite this