Optimization of VUV characteristics and morphology of BaMgAl10O17:Eu2+ phosphor particles in spray pyrolysis

Y. C. Kang, H. S. Roh, H. D. Park, S. B. Park

Research output: Contribution to journalArticle

30 Citations (Scopus)

Abstract

The VUV characteristics of BaMgAl10O17:Eu2+ phosphor particles prepared by an ultrasonic spray pyrolysis were compared with those of commercial product. The precursor effect on the morphology and brightness of phosphor particles was investigated in spray pyrolysis. The phosphor particles were prepared from 24 combinations of barium, magnesium, and aluminum component precursors composing host material. The precursor types strongly affected the morphology and luminescence characteristics of BAM phosphor particles. The BAM phosphor particles posttreated at above 1250 °C had higher brightness than that of commercial product. The maximum brightness of particles obtained at 1350 °C from nitrate precursors was 109% that of commercial product. This optimum posttreatment temperature in spray pyrolysis is lower than that of conventional solid-state reaction method.

Original languageEnglish
Pages (from-to)41-47
Number of pages7
JournalCeramics International
Volume29
Issue number1
DOIs
Publication statusPublished - 2003
Externally publishedYes

Keywords

  • A. Powders: gas phase reaction
  • A. Precursors
  • C. Optical properties

ASJC Scopus subject areas

  • Electronic, Optical and Magnetic Materials
  • Ceramics and Composites
  • Process Chemistry and Technology
  • Surfaces, Coatings and Films
  • Materials Chemistry

Fingerprint Dive into the research topics of 'Optimization of VUV characteristics and morphology of BaMgAl<sub>10</sub>O<sub>17</sub>:Eu<sup>2+</sup> phosphor particles in spray pyrolysis'. Together they form a unique fingerprint.

  • Cite this