Research on carbon-coated Li 4Ti 5O 12 material for lithium ion batteries

Ju Bin Kim, Dong Jin Kim, Kyung Yoon Chung, Dong Jin Byun, Byung Won Cho

Research output: Chapter in Book/Report/Conference proceedingConference contribution

23 Citations (Scopus)

Abstract

Carbon-coated Li 4Ti 5O 12 anode materials for the lithium ion battery were synthesized by using sucrose to improve the electrochemical properties of Li 4Ti 5O 12, and the carbon content was then tested. X-ray diffraction (XRD) showed that the coating of carbon does not influence the formation of Li 4Ti 5O 12. Transmission electron microscopy (TEM) and Raman spectroscopy confirmed that carbon content exists on the surface of Li 4Ti 5O 12. Electronic conductivity measurement indicated that the electronic conductivity of the carbon-coated Li 4Ti 5O 12 material was 3.8×10 -4 S cm -1, which is higher than that for the primary Li 4Ti 5O 12 material (4.3×10 -7 S cm -1). CV results show that carbon-coated Li 4Ti 5O 12 shows a larger diffusion coefficient. Charge and discharge tests show that rate capability and cycle performance were improved because of the carbon coating.

Original languageEnglish
Title of host publicationPhysica Scripta T
VolumeT139
DOIs
Publication statusPublished - 2010
Event3rd International Symposium on Functional Materials 2009, ISFM 2009 - Jinju, Korea, Republic of
Duration: 2009 Jun 152009 Jun 18

Other

Other3rd International Symposium on Functional Materials 2009, ISFM 2009
CountryKorea, Republic of
CityJinju
Period09/6/1509/6/18

Fingerprint

electric batteries
lithium
carbon
ions
conductivity
sucrose
electronics
coating
anodes
diffusion coefficient
Raman spectroscopy
coatings
transmission electron microscopy
cycles
diffraction
x rays

ASJC Scopus subject areas

  • Physics and Astronomy(all)

Cite this

Kim, J. B., Kim, D. J., Chung, K. Y., Byun, D. J., & Cho, B. W. (2010). Research on carbon-coated Li 4Ti 5O 12 material for lithium ion batteries In Physica Scripta T (Vol. T139). [014026] https://doi.org/10.1088/0031-8949/2010/T139/014026

Research on carbon-coated Li 4Ti 5O 12 material for lithium ion batteries . / Kim, Ju Bin; Kim, Dong Jin; Chung, Kyung Yoon; Byun, Dong Jin; Cho, Byung Won.

Physica Scripta T. Vol. T139 2010. 014026.

Research output: Chapter in Book/Report/Conference proceedingConference contribution

Kim, JB, Kim, DJ, Chung, KY, Byun, DJ & Cho, BW 2010, Research on carbon-coated Li 4Ti 5O 12 material for lithium ion batteries in Physica Scripta T. vol. T139, 014026, 3rd International Symposium on Functional Materials 2009, ISFM 2009, Jinju, Korea, Republic of, 09/6/15. https://doi.org/10.1088/0031-8949/2010/T139/014026
Kim, Ju Bin ; Kim, Dong Jin ; Chung, Kyung Yoon ; Byun, Dong Jin ; Cho, Byung Won. / Research on carbon-coated Li 4Ti 5O 12 material for lithium ion batteries Physica Scripta T. Vol. T139 2010.
@inproceedings{1c834b1cf9494fd5957ba29e94d18148,
title = "Research on carbon-coated Li 4Ti 5O 12 material for lithium ion batteries",
abstract = "Carbon-coated Li 4Ti 5O 12 anode materials for the lithium ion battery were synthesized by using sucrose to improve the electrochemical properties of Li 4Ti 5O 12, and the carbon content was then tested. X-ray diffraction (XRD) showed that the coating of carbon does not influence the formation of Li 4Ti 5O 12. Transmission electron microscopy (TEM) and Raman spectroscopy confirmed that carbon content exists on the surface of Li 4Ti 5O 12. Electronic conductivity measurement indicated that the electronic conductivity of the carbon-coated Li 4Ti 5O 12 material was 3.8×10 -4 S cm -1, which is higher than that for the primary Li 4Ti 5O 12 material (4.3×10 -7 S cm -1). CV results show that carbon-coated Li 4Ti 5O 12 shows a larger diffusion coefficient. Charge and discharge tests show that rate capability and cycle performance were improved because of the carbon coating.",
author = "Kim, {Ju Bin} and Kim, {Dong Jin} and Chung, {Kyung Yoon} and Byun, {Dong Jin} and Cho, {Byung Won}",
year = "2010",
doi = "10.1088/0031-8949/2010/T139/014026",
language = "English",
volume = "T139",
booktitle = "Physica Scripta T",

}

TY - GEN

T1 - Research on carbon-coated Li 4Ti 5O 12 material for lithium ion batteries

AU - Kim, Ju Bin

AU - Kim, Dong Jin

AU - Chung, Kyung Yoon

AU - Byun, Dong Jin

AU - Cho, Byung Won

PY - 2010

Y1 - 2010

N2 - Carbon-coated Li 4Ti 5O 12 anode materials for the lithium ion battery were synthesized by using sucrose to improve the electrochemical properties of Li 4Ti 5O 12, and the carbon content was then tested. X-ray diffraction (XRD) showed that the coating of carbon does not influence the formation of Li 4Ti 5O 12. Transmission electron microscopy (TEM) and Raman spectroscopy confirmed that carbon content exists on the surface of Li 4Ti 5O 12. Electronic conductivity measurement indicated that the electronic conductivity of the carbon-coated Li 4Ti 5O 12 material was 3.8×10 -4 S cm -1, which is higher than that for the primary Li 4Ti 5O 12 material (4.3×10 -7 S cm -1). CV results show that carbon-coated Li 4Ti 5O 12 shows a larger diffusion coefficient. Charge and discharge tests show that rate capability and cycle performance were improved because of the carbon coating.

AB - Carbon-coated Li 4Ti 5O 12 anode materials for the lithium ion battery were synthesized by using sucrose to improve the electrochemical properties of Li 4Ti 5O 12, and the carbon content was then tested. X-ray diffraction (XRD) showed that the coating of carbon does not influence the formation of Li 4Ti 5O 12. Transmission electron microscopy (TEM) and Raman spectroscopy confirmed that carbon content exists on the surface of Li 4Ti 5O 12. Electronic conductivity measurement indicated that the electronic conductivity of the carbon-coated Li 4Ti 5O 12 material was 3.8×10 -4 S cm -1, which is higher than that for the primary Li 4Ti 5O 12 material (4.3×10 -7 S cm -1). CV results show that carbon-coated Li 4Ti 5O 12 shows a larger diffusion coefficient. Charge and discharge tests show that rate capability and cycle performance were improved because of the carbon coating.

UR - http://www.scopus.com/inward/record.url?scp=77954723340&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=77954723340&partnerID=8YFLogxK

U2 - 10.1088/0031-8949/2010/T139/014026

DO - 10.1088/0031-8949/2010/T139/014026

M3 - Conference contribution

AN - SCOPUS:77954723340

VL - T139

BT - Physica Scripta T

ER -