Silver coated cathodes for MCFC and their characteristic

Shin Ae Song, Jonghee Han, Sung Pil Yoon, In Hwan Oh, SukWoo Nam, Tae Hoon Lim

Research output: Chapter in Book/Report/Conference proceedingConference contribution

Abstract

Ag coated NiO cathode for MCFC was prepared using nano Ag sol in order to improve the cathode polarization at low temperature. It was confirmed that Ag is well dispersed on the porous Ni plate by SEM. Ag coated cathode NiO shows the higher performance of 0.8V at current density of 150mA/cm2 and 600°C compared with that of uncoated cathode of 0.76V. EIS analysis shows that the charge transfer resistance is reduced dramatically by Ag coating, which might result from the catalytic effect of Ag.

Original languageEnglish
Title of host publicationEFC 2011 - Proceedings of the 4th European Fuel Cell Piero Lunghi Conference and Exhibition
PublisherENEA
Pages103-104
Number of pages2
ISBN (Print)9788882862541
Publication statusPublished - 2011
Externally publishedYes
Event4th European Fuel Cell Piero Lunghi Conference and Exhibition, EFC 2011 - Rome, Italy
Duration: 2011 Dec 142011 Dec 16

Other

Other4th European Fuel Cell Piero Lunghi Conference and Exhibition, EFC 2011
CountryItaly
CityRome
Period11/12/1411/12/16

Fingerprint

Molten carbonate fuel cells (MCFC)
Silver
Cathodes
Sols
Charge transfer
Current density
Polarization
Coatings
Scanning electron microscopy
Temperature

ASJC Scopus subject areas

  • Fuel Technology

Cite this

Song, S. A., Han, J., Yoon, S. P., Oh, I. H., Nam, S., & Lim, T. H. (2011). Silver coated cathodes for MCFC and their characteristic. In EFC 2011 - Proceedings of the 4th European Fuel Cell Piero Lunghi Conference and Exhibition (pp. 103-104). ENEA.

Silver coated cathodes for MCFC and their characteristic. / Song, Shin Ae; Han, Jonghee; Yoon, Sung Pil; Oh, In Hwan; Nam, SukWoo; Lim, Tae Hoon.

EFC 2011 - Proceedings of the 4th European Fuel Cell Piero Lunghi Conference and Exhibition. ENEA, 2011. p. 103-104.

Research output: Chapter in Book/Report/Conference proceedingConference contribution

Song, SA, Han, J, Yoon, SP, Oh, IH, Nam, S & Lim, TH 2011, Silver coated cathodes for MCFC and their characteristic. in EFC 2011 - Proceedings of the 4th European Fuel Cell Piero Lunghi Conference and Exhibition. ENEA, pp. 103-104, 4th European Fuel Cell Piero Lunghi Conference and Exhibition, EFC 2011, Rome, Italy, 11/12/14.
Song SA, Han J, Yoon SP, Oh IH, Nam S, Lim TH. Silver coated cathodes for MCFC and their characteristic. In EFC 2011 - Proceedings of the 4th European Fuel Cell Piero Lunghi Conference and Exhibition. ENEA. 2011. p. 103-104
Song, Shin Ae ; Han, Jonghee ; Yoon, Sung Pil ; Oh, In Hwan ; Nam, SukWoo ; Lim, Tae Hoon. / Silver coated cathodes for MCFC and their characteristic. EFC 2011 - Proceedings of the 4th European Fuel Cell Piero Lunghi Conference and Exhibition. ENEA, 2011. pp. 103-104
@inproceedings{01938f865767478c993dd21ac69b8aec,
title = "Silver coated cathodes for MCFC and their characteristic",
abstract = "Ag coated NiO cathode for MCFC was prepared using nano Ag sol in order to improve the cathode polarization at low temperature. It was confirmed that Ag is well dispersed on the porous Ni plate by SEM. Ag coated cathode NiO shows the higher performance of 0.8V at current density of 150mA/cm2 and 600°C compared with that of uncoated cathode of 0.76V. EIS analysis shows that the charge transfer resistance is reduced dramatically by Ag coating, which might result from the catalytic effect of Ag.",
author = "Song, {Shin Ae} and Jonghee Han and Yoon, {Sung Pil} and Oh, {In Hwan} and SukWoo Nam and Lim, {Tae Hoon}",
year = "2011",
language = "English",
isbn = "9788882862541",
pages = "103--104",
booktitle = "EFC 2011 - Proceedings of the 4th European Fuel Cell Piero Lunghi Conference and Exhibition",
publisher = "ENEA",

}

TY - GEN

T1 - Silver coated cathodes for MCFC and their characteristic

AU - Song, Shin Ae

AU - Han, Jonghee

AU - Yoon, Sung Pil

AU - Oh, In Hwan

AU - Nam, SukWoo

AU - Lim, Tae Hoon

PY - 2011

Y1 - 2011

N2 - Ag coated NiO cathode for MCFC was prepared using nano Ag sol in order to improve the cathode polarization at low temperature. It was confirmed that Ag is well dispersed on the porous Ni plate by SEM. Ag coated cathode NiO shows the higher performance of 0.8V at current density of 150mA/cm2 and 600°C compared with that of uncoated cathode of 0.76V. EIS analysis shows that the charge transfer resistance is reduced dramatically by Ag coating, which might result from the catalytic effect of Ag.

AB - Ag coated NiO cathode for MCFC was prepared using nano Ag sol in order to improve the cathode polarization at low temperature. It was confirmed that Ag is well dispersed on the porous Ni plate by SEM. Ag coated cathode NiO shows the higher performance of 0.8V at current density of 150mA/cm2 and 600°C compared with that of uncoated cathode of 0.76V. EIS analysis shows that the charge transfer resistance is reduced dramatically by Ag coating, which might result from the catalytic effect of Ag.

UR - http://www.scopus.com/inward/record.url?scp=84923592689&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=84923592689&partnerID=8YFLogxK

M3 - Conference contribution

SN - 9788882862541

SP - 103

EP - 104

BT - EFC 2011 - Proceedings of the 4th European Fuel Cell Piero Lunghi Conference and Exhibition

PB - ENEA

ER -