Sintering behavior and dielectric properties of KCa2Nb3O10 ceramics

Sang Hyo Kweon, Mir Im, Guifang Han, Jin Seong Kim, Sahn Nahm, Ji Won Choi, Seong Ju Hwang

Research output: Contribution to journalArticle

8 Citations (Scopus)

Abstract

Dense KCa2Nb3O10 (KCN) oxides were synthesized and their dielectric properties were investigated. A homogeneous KCN phase was formed in the specimen sintered above 1300°C, but a CaNb2O6 secondary phase was developed in the specimen sintered at 1400°C, as result of the evaporation of K2O. The KCN oxides sintered at 1375°C showed a high relative density that was 97.1% of the theoretical density. Furthermore, liquid-phase-assisted abnormal grain growth occurred during sintering. The dielectric constant of this KCN oxide was 46, with a low dielectric loss of 0.9% at 100kHz; these values are smaller than those that were previously reported. Complex impedance analysis indicated that the resistivity of the KCN oxide was very low, probably as a result of the presence of K+ ions between the layers, and this could be the origin of the low-frequency dispersion of the KCN oxides.

Original languageEnglish
Pages (from-to)907-911
Number of pages5
JournalJournal of the European Ceramic Society
Volume33
Issue number5
DOIs
Publication statusPublished - 2013 May 1

Keywords

  • Dielectrics
  • Layered perovskite
  • Low loss
  • Multilayer ceramic capacitor

ASJC Scopus subject areas

  • Ceramics and Composites
  • Materials Chemistry

Fingerprint Dive into the research topics of 'Sintering behavior and dielectric properties of KCa<sub>2</sub>Nb<sub>3</sub>O<sub>10</sub> ceramics'. Together they form a unique fingerprint.

  • Cite this