The characteristics of X1 type Y2SiO5:Tb phosphor particles prepared by high temperature spray pyrolysis

H. J. Lee, S. K. Hong, D. S. Jung, S. H. Ju, H. Y. Koo, Yun Chan Kang

Research output: Contribution to journalArticle

16 Citations (Scopus)

Abstract

The X1 type Y2SiO5:Tb phosphor particles with high brightness were prepared by spray pyrolysis from spray solution with NH4F flux material. The phosphor particles prepared by spray pyrolysis at high preparation temperature had spherical shape, fine size and dense morphology. The mean sizes of the phosphor particles prepared at 900 and 1650 °C were 1.3 and 0.9 μm. The emission spectrum of the phosphor particles prepared by spray pyrolysis at 1650oC had the characteristics of X1 type Y2SiO5:Tb phosphor. The photoluminescence intensity of the phosphor particles directly prepared by spray pyrolysis from spray solution with 20 wt.% NH4F flux of the product at temperature of 1650 °C was 127 and 184% of the X1 and X2 type Y2SiO5:Tb phosphor particles post-treated at 1100 and 1300 °C, respectively. The Y2SiO5:Tb phosphor particles prepared by spray pyrolysis at 1650 °C had X1 type crystal structure because of short residence time of particles inside hot wall reactor of 0.4 s.

Original languageEnglish
Pages (from-to)865-870
Number of pages6
JournalCeramics International
Volume32
Issue number8
DOIs
Publication statusPublished - 2006 Dec 1
Externally publishedYes

Fingerprint

Spray pyrolysis
Phosphors
Temperature
Fluxes
Luminance
Photoluminescence
Crystal structure

Keywords

  • A. Powders: gas phase reaction
  • C. Optical properties

ASJC Scopus subject areas

  • Electronic, Optical and Magnetic Materials
  • Ceramics and Composites
  • Process Chemistry and Technology
  • Surfaces, Coatings and Films
  • Materials Chemistry

Cite this

The characteristics of X1 type Y2SiO5:Tb phosphor particles prepared by high temperature spray pyrolysis. / Lee, H. J.; Hong, S. K.; Jung, D. S.; Ju, S. H.; Koo, H. Y.; Kang, Yun Chan.

In: Ceramics International, Vol. 32, No. 8, 01.12.2006, p. 865-870.

Research output: Contribution to journalArticle

Lee, H. J. ; Hong, S. K. ; Jung, D. S. ; Ju, S. H. ; Koo, H. Y. ; Kang, Yun Chan. / The characteristics of X1 type Y2SiO5:Tb phosphor particles prepared by high temperature spray pyrolysis. In: Ceramics International. 2006 ; Vol. 32, No. 8. pp. 865-870.
@article{3bd46df3fee047aa99f8582305fa633c,
title = "The characteristics of X1 type Y2SiO5:Tb phosphor particles prepared by high temperature spray pyrolysis",
abstract = "The X1 type Y2SiO5:Tb phosphor particles with high brightness were prepared by spray pyrolysis from spray solution with NH4F flux material. The phosphor particles prepared by spray pyrolysis at high preparation temperature had spherical shape, fine size and dense morphology. The mean sizes of the phosphor particles prepared at 900 and 1650 °C were 1.3 and 0.9 μm. The emission spectrum of the phosphor particles prepared by spray pyrolysis at 1650oC had the characteristics of X1 type Y2SiO5:Tb phosphor. The photoluminescence intensity of the phosphor particles directly prepared by spray pyrolysis from spray solution with 20 wt.{\%} NH4F flux of the product at temperature of 1650 °C was 127 and 184{\%} of the X1 and X2 type Y2SiO5:Tb phosphor particles post-treated at 1100 and 1300 °C, respectively. The Y2SiO5:Tb phosphor particles prepared by spray pyrolysis at 1650 °C had X1 type crystal structure because of short residence time of particles inside hot wall reactor of 0.4 s.",
keywords = "A. Powders: gas phase reaction, C. Optical properties",
author = "Lee, {H. J.} and Hong, {S. K.} and Jung, {D. S.} and Ju, {S. H.} and Koo, {H. Y.} and Kang, {Yun Chan}",
year = "2006",
month = "12",
day = "1",
doi = "10.1016/j.ceramint.2005.07.001",
language = "English",
volume = "32",
pages = "865--870",
journal = "Ceramics International",
issn = "0272-8842",
publisher = "Elsevier Limited",
number = "8",

}

TY - JOUR

T1 - The characteristics of X1 type Y2SiO5:Tb phosphor particles prepared by high temperature spray pyrolysis

AU - Lee, H. J.

AU - Hong, S. K.

AU - Jung, D. S.

AU - Ju, S. H.

AU - Koo, H. Y.

AU - Kang, Yun Chan

PY - 2006/12/1

Y1 - 2006/12/1

N2 - The X1 type Y2SiO5:Tb phosphor particles with high brightness were prepared by spray pyrolysis from spray solution with NH4F flux material. The phosphor particles prepared by spray pyrolysis at high preparation temperature had spherical shape, fine size and dense morphology. The mean sizes of the phosphor particles prepared at 900 and 1650 °C were 1.3 and 0.9 μm. The emission spectrum of the phosphor particles prepared by spray pyrolysis at 1650oC had the characteristics of X1 type Y2SiO5:Tb phosphor. The photoluminescence intensity of the phosphor particles directly prepared by spray pyrolysis from spray solution with 20 wt.% NH4F flux of the product at temperature of 1650 °C was 127 and 184% of the X1 and X2 type Y2SiO5:Tb phosphor particles post-treated at 1100 and 1300 °C, respectively. The Y2SiO5:Tb phosphor particles prepared by spray pyrolysis at 1650 °C had X1 type crystal structure because of short residence time of particles inside hot wall reactor of 0.4 s.

AB - The X1 type Y2SiO5:Tb phosphor particles with high brightness were prepared by spray pyrolysis from spray solution with NH4F flux material. The phosphor particles prepared by spray pyrolysis at high preparation temperature had spherical shape, fine size and dense morphology. The mean sizes of the phosphor particles prepared at 900 and 1650 °C were 1.3 and 0.9 μm. The emission spectrum of the phosphor particles prepared by spray pyrolysis at 1650oC had the characteristics of X1 type Y2SiO5:Tb phosphor. The photoluminescence intensity of the phosphor particles directly prepared by spray pyrolysis from spray solution with 20 wt.% NH4F flux of the product at temperature of 1650 °C was 127 and 184% of the X1 and X2 type Y2SiO5:Tb phosphor particles post-treated at 1100 and 1300 °C, respectively. The Y2SiO5:Tb phosphor particles prepared by spray pyrolysis at 1650 °C had X1 type crystal structure because of short residence time of particles inside hot wall reactor of 0.4 s.

KW - A. Powders: gas phase reaction

KW - C. Optical properties

UR - http://www.scopus.com/inward/record.url?scp=33748412854&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=33748412854&partnerID=8YFLogxK

U2 - 10.1016/j.ceramint.2005.07.001

DO - 10.1016/j.ceramint.2005.07.001

M3 - Article

AN - SCOPUS:33748412854

VL - 32

SP - 865

EP - 870

JO - Ceramics International

JF - Ceramics International

SN - 0272-8842

IS - 8

ER -