T1 - Three-Dimensional Flexible All-Organic Conductors for Multifunctional Wearable Applications
AU - Moon, In Kyu
AU - Yoon, Seonno
AU - Lee, Hee Uk
AU - Kim, Seung Wook
AU - Oh, Jungwoo
PY - 2017/11/22
Y1 - 2017/11/22
N2 - Wearable textile electrodes based on π-conjugated polymers are appealing alternatives to carbon fabrics, conductive yarns, or metal wires because of their design flexibility, low cost, flexibility, and high throughput. This provides the benefits of both electronics and textiles. Herein, a general and new method has been developed to produce tailorable, wearable energy devices that are based on three-dimensional (3D) poly(3,4-ethylenedioxythiophene) (PEDOT)-coated textile conductors. To obtain the desired electrode materials, both facile solution-dropping polymerization methods are used to fabricate a 3D flexible PEDOT conductor on a cotton textile (PEDOT/textile). PEDOT/textile shows a very low sheet resistance of 4.6-4.9 ω·sq-1. Here, we employ the example of this 3D network-like structure and the excellent electrical conductivities under the large deformation of PEDOT/textiles to show that wearable and portable heaters have immense potential. A flexible textile heater with a large area (8 × 7.8 cm2) reached a saturation temperature of ∼83.9 °C when a bias of 7 V was applied for ∼70 s due to the good electrical conductivity of PEDOT. To demonstrate the performance of all-solid-state supercapacitors, nano-ascidian-like PEDOT (PEDOT-NA) arrays were prepared via a simple vapor-phase polymerization of 3,4-ethylenedioxythiophene on PEDOT/textile to increase both the surface area and the number of ion diffusion paths. The PEDOT-NA arrays on PEDOT/textile showed outstanding performance with an areal capacitance of 563.3 mF·cm-2 at 0.4 mA·cm-2 and extraordinary mechanical flexibility. The maximum volumetric power density and energy density of the nanostructured PEDOT on the textile were 1.75 W·cm-3 and 0.0812 Wh·cm-3, respectively. It is expected that the wearable nanostructured conducting polymers will have advantages when used as structures for smart textronics and energy conversion/storage.
AB - Wearable textile electrodes based on π-conjugated polymers are appealing alternatives to carbon fabrics, conductive yarns, or metal wires because of their design flexibility, low cost, flexibility, and high throughput. This provides the benefits of both electronics and textiles. Herein, a general and new method has been developed to produce tailorable, wearable energy devices that are based on three-dimensional (3D) poly(3,4-ethylenedioxythiophene) (PEDOT)-coated textile conductors. To obtain the desired electrode materials, both facile solution-dropping polymerization methods are used to fabricate a 3D flexible PEDOT conductor on a cotton textile (PEDOT/textile). PEDOT/textile shows a very low sheet resistance of 4.6-4.9 ω·sq-1. Here, we employ the example of this 3D network-like structure and the excellent electrical conductivities under the large deformation of PEDOT/textiles to show that wearable and portable heaters have immense potential. A flexible textile heater with a large area (8 × 7.8 cm2) reached a saturation temperature of ∼83.9 °C when a bias of 7 V was applied for ∼70 s due to the good electrical conductivity of PEDOT. To demonstrate the performance of all-solid-state supercapacitors, nano-ascidian-like PEDOT (PEDOT-NA) arrays were prepared via a simple vapor-phase polymerization of 3,4-ethylenedioxythiophene on PEDOT/textile to increase both the surface area and the number of ion diffusion paths. The PEDOT-NA arrays on PEDOT/textile showed outstanding performance with an areal capacitance of 563.3 mF·cm-2 at 0.4 mA·cm-2 and extraordinary mechanical flexibility. The maximum volumetric power density and energy density of the nanostructured PEDOT on the textile were 1.75 W·cm-3 and 0.0812 Wh·cm-3, respectively. It is expected that the wearable nanostructured conducting polymers will have advantages when used as structures for smart textronics and energy conversion/storage.
KW - all-organic devices
KW - all-solid-state supercapacitors
KW - conducting polymers
KW - thermal managements
KW - wearable electronics
UR - http://www.scopus.com/inward/record.url?scp=85034992950&partnerID=8YFLogxK
UR - http://www.scopus.com/inward/citedby.url?scp=85034992950&partnerID=8YFLogxK
U2 - 10.1021/acsami.7b10181
DO - 10.1021/acsami.7b10181
M3 - Article
C2 - 29067808
AN - SCOPUS:85034992950
VL - 9
SP - 40580
EP - 40592
JO - ACS applied materials & interfaces
JF - ACS applied materials & interfaces
SN - 1944-8244
IS - 46
ER -