Total Dose Effects and Single Event Upsets during Radiation Damage of GaN and SiC

Ani Khachatrian, Adrian Ildefonso, Zahabul Islam, Md Abu Jafar Rasel, Amanul Haque, Jihyun Kim, Fan Ren, Minghan Xian, Stephen J. Pearton

Research output: Chapter in Book/Report/Conference proceedingConference contribution

Abstract

SiC and GaN power devices are used in the automotive, wireless, and industrial power markets, but their adoption into space and avionic applications is hindered by their susceptibility to permanent degradation and catastrophic failure from heavy-ion exposure. Efforts to space-qualify wide bandgap power devices have revealed that they are susceptible to damage from the high-energy, heavy-ion space radiation environment (galactic cosmic rays) that cannot be shielded. GaN and SiC transistors have shown failure susceptibility at about 50% of the rated voltage. SiC components have demonstrated susceptibility to radiation damage under heavy-ion single-event effects testing, reducing their utility in the space galactic cosmic ray (GCR) environment. In SiC-based Schottky diodes, catastrophic single-event burnout (SEB) and other single-event effects (SEE) have been observed at ∼40% of the rated operating voltage, as well as an unacceptable degradation in leakage current at ∼20% of the rated operating voltage.

Original languageEnglish
Title of host publication240th ECS Meeting - Gallium Nitride and Silicon Carbide Power Technologies 11
PublisherIOP Publishing Ltd.
Pages13-34
Number of pages22
Edition7
ISBN (Electronic)9781607685395
DOIs
Publication statusPublished - 2021
Event240th ECS Meeting - Orlando, United States
Duration: 2021 Oct 102021 Oct 14

Publication series

NameECS Transactions
Number7
Volume104
ISSN (Print)1938-6737
ISSN (Electronic)1938-5862

Conference

Conference240th ECS Meeting
Country/TerritoryUnited States
CityOrlando
Period21/10/1021/10/14

ASJC Scopus subject areas

  • Engineering(all)

Fingerprint

Dive into the research topics of 'Total Dose Effects and Single Event Upsets during Radiation Damage of GaN and SiC'. Together they form a unique fingerprint.

Cite this