Variations in electrical properties of Nb-doped SrTiO 3 with cation nonstoichiometry

Jung Ho Moon, Seong Ho Kim, Keun Il Park, Yoonho Kim, Keon Kim

Research output: Chapter in Book/Report/Conference proceedingConference contribution

Abstract

The influences of Sr/(Ti+Nb) ratios on the electrical properties of Nb-doped SrTiO 3 ceramics have been investigated. Regardless of Sr/(Ti+Nb) ratios, the appearance of non-linearity in the current-voltage characteristics was observed. When Sr/(Ti+Nb) ratio is lower than 1.000, the results acquired from impedance analysis revealed that the activation energies for carrier conduction were determined to be 0.83 eV in grains and 1.67 eV in grain boundaries. Otherwise, the specimens with Sr/(Ti+Nb) ≥ 1.004 showed energies of 0.80 eV in grains and 1.27 eV in grain boundaries. From these measured results, it was suggested that the activation energies, about 0.80 eV, measured in grains were originated from oxygen vacancies and the activation energies, 1.27 and 1.67 eV, measured in grain boundaries were from titanium and strontium vacancies, respectively.

Original languageEnglish
Title of host publicationFerroelectrics
Pages267-272
Number of pages6
Volume269
DOIs
Publication statusPublished - 2002 Jan 1

Fingerprint

Cations
Grain boundaries
Electric properties
grain boundaries
Activation energy
Positive ions
electrical properties
activation energy
cations
Strontium
Oxygen vacancies
Current voltage characteristics
Titanium
strontium
Vacancies
titanium
nonlinearity
impedance
ceramics
conduction

ASJC Scopus subject areas

  • Materials Science(all)
  • Condensed Matter Physics
  • Electronic, Optical and Magnetic Materials

Cite this

Moon, J. H., Kim, S. H., Park, K. I., Kim, Y., & Kim, K. (2002). Variations in electrical properties of Nb-doped SrTiO 3 with cation nonstoichiometry In Ferroelectrics (Vol. 269, pp. 267-272) https://doi.org/10.1080/00150190211166

Variations in electrical properties of Nb-doped SrTiO 3 with cation nonstoichiometry . / Moon, Jung Ho; Kim, Seong Ho; Park, Keun Il; Kim, Yoonho; Kim, Keon.

Ferroelectrics. Vol. 269 2002. p. 267-272.

Research output: Chapter in Book/Report/Conference proceedingConference contribution

Moon, Jung Ho ; Kim, Seong Ho ; Park, Keun Il ; Kim, Yoonho ; Kim, Keon. / Variations in electrical properties of Nb-doped SrTiO 3 with cation nonstoichiometry Ferroelectrics. Vol. 269 2002. pp. 267-272
@inproceedings{d5418713f6c540d5aa9844bb87b0f845,
title = "Variations in electrical properties of Nb-doped SrTiO 3 with cation nonstoichiometry",
abstract = "The influences of Sr/(Ti+Nb) ratios on the electrical properties of Nb-doped SrTiO 3 ceramics have been investigated. Regardless of Sr/(Ti+Nb) ratios, the appearance of non-linearity in the current-voltage characteristics was observed. When Sr/(Ti+Nb) ratio is lower than 1.000, the results acquired from impedance analysis revealed that the activation energies for carrier conduction were determined to be 0.83 eV in grains and 1.67 eV in grain boundaries. Otherwise, the specimens with Sr/(Ti+Nb) ≥ 1.004 showed energies of 0.80 eV in grains and 1.27 eV in grain boundaries. From these measured results, it was suggested that the activation energies, about 0.80 eV, measured in grains were originated from oxygen vacancies and the activation energies, 1.27 and 1.67 eV, measured in grain boundaries were from titanium and strontium vacancies, respectively.",
author = "Moon, {Jung Ho} and Kim, {Seong Ho} and Park, {Keun Il} and Yoonho Kim and Keon Kim",
year = "2002",
month = "1",
day = "1",
doi = "10.1080/00150190211166",
language = "English",
volume = "269",
pages = "267--272",
booktitle = "Ferroelectrics",

}

TY - GEN

T1 - Variations in electrical properties of Nb-doped SrTiO 3 with cation nonstoichiometry

AU - Moon, Jung Ho

AU - Kim, Seong Ho

AU - Park, Keun Il

AU - Kim, Yoonho

AU - Kim, Keon

PY - 2002/1/1

Y1 - 2002/1/1

N2 - The influences of Sr/(Ti+Nb) ratios on the electrical properties of Nb-doped SrTiO 3 ceramics have been investigated. Regardless of Sr/(Ti+Nb) ratios, the appearance of non-linearity in the current-voltage characteristics was observed. When Sr/(Ti+Nb) ratio is lower than 1.000, the results acquired from impedance analysis revealed that the activation energies for carrier conduction were determined to be 0.83 eV in grains and 1.67 eV in grain boundaries. Otherwise, the specimens with Sr/(Ti+Nb) ≥ 1.004 showed energies of 0.80 eV in grains and 1.27 eV in grain boundaries. From these measured results, it was suggested that the activation energies, about 0.80 eV, measured in grains were originated from oxygen vacancies and the activation energies, 1.27 and 1.67 eV, measured in grain boundaries were from titanium and strontium vacancies, respectively.

AB - The influences of Sr/(Ti+Nb) ratios on the electrical properties of Nb-doped SrTiO 3 ceramics have been investigated. Regardless of Sr/(Ti+Nb) ratios, the appearance of non-linearity in the current-voltage characteristics was observed. When Sr/(Ti+Nb) ratio is lower than 1.000, the results acquired from impedance analysis revealed that the activation energies for carrier conduction were determined to be 0.83 eV in grains and 1.67 eV in grain boundaries. Otherwise, the specimens with Sr/(Ti+Nb) ≥ 1.004 showed energies of 0.80 eV in grains and 1.27 eV in grain boundaries. From these measured results, it was suggested that the activation energies, about 0.80 eV, measured in grains were originated from oxygen vacancies and the activation energies, 1.27 and 1.67 eV, measured in grain boundaries were from titanium and strontium vacancies, respectively.

UR - http://www.scopus.com/inward/record.url?scp=33746296191&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=33746296191&partnerID=8YFLogxK

U2 - 10.1080/00150190211166

DO - 10.1080/00150190211166

M3 - Conference contribution

AN - SCOPUS:33746296191

VL - 269

SP - 267

EP - 272

BT - Ferroelectrics

ER -